Near-infrared broadband luminescence of Yb-doped PbClF crystals
Near-infrared broadband luminescence of Yb-doped PbClF crystals
复制标题
Yb 掺杂 PbClF 晶体的近红外宽带发光
DOI：
10.1016/j.jlumin.2012.02.029
复制
发表时间：
2012-09
影响因子：
3.6
通讯作者：
Qian, Guoxing
中科院分区：
文献类型：
--
作者：
Xu, Jun;Su, Liangbi;Li, Hongjun;Zheng, Lihe;Xu, Xiaodong;Wu, Feng;Tang, Huili;Jiang, Dapeng;Qian, Guoxing
采用改进的Bridgman法制备了掺Yb的PbClF晶体。在掺2.0%Yb ~（3+）的PbClF晶体中观察到了宽带发射（FWHM= 58 nm）和长寿命（5.33ms）。计算得到掺Yb ~（3+）0.5%PbClF晶体中Yb ~（3+）2F ~（7/2）能级的斯塔克分裂为801 cm-1，相应的低激光能级的布居数约为2.13%。结果表明，掺Yb的PbClF晶体是一种很有前途的1.0μm超短脉冲输出材料。
Yb-doped PbClF crystals were obtained by a modified Bridgman method. Broadband emission (FWHM=58nm) with long lifetime (5.33ms) was observed in 2.0% Yb3+-doped PbClF crystals. The Stark splitting of Yb3+2F7/2level was calculated to be 801cm−1in 0.5% Yb3+-doped PbClF crystals, and the corresponding population of lower laser level is about 2.13%. All the results indicated that Yb-doped PbClF crystals should be a promising material to ultrashort pulses output at 1.0μm.
登录
查看更多内容
DOI：
10.1007/s00340-004-1561-z
发表时间：
2004-06
期刊：
Applied Physics B
影响因子：
--
作者：
G. Paunescu;J. Hein;R. Sauerbrey
通讯作者：
G. Paunescu;J. Hein;R. Sauerbrey
影响因子：
3.7
作者：
CORISH, J;CATLOW, CRA;ONG, SH
通讯作者：
ONG, SH
影响因子：
3.6
作者：
M. Siebold;M. Hornung;R. Boedefeld;S. Podleska;S. Klingebiel;C. Wandt;F. Krausz;S. Karsch;R. Uecker;A. Jochmann;J. Hein;M. Kaluza
通讯作者：
M. Siebold;M. Hornung;R. Boedefeld;S. Podleska;S. Klingebiel;C. Wandt;F. Krausz;S. Karsch;R. Uecker;A. Jochmann;J. Hein;M. Kaluza
影响因子：
3.6
作者：
Jigang Yin;Y. Hang;X. Liang;Xiaoming He;Jinfeng Li;Lianhang Zhang;Chengchun Zhao;P. Hu
通讯作者：
Jigang Yin;Y. Hang;X. Liang;Xiaoming He;Jinfeng Li;Lianhang Zhang;Chengchun Zhao;P. Hu
DOI：
10.1007/bf00516262
发表时间：
1966-03
期刊：
Fresenius' Zeitschrift für analytische Chemie
影响因子：
--
作者：
C. Harzdorf;Ottmar Steinhauser
通讯作者：
C. Harzdorf;Ottmar Steinhauser