Effect of Ag addition on local structure of Cu–Zr glassy alloy
Effect of Ag addition on local structure of Cu–Zr glassy alloy
复制标题
Ag添加对Cu-Zr非晶合金局部结构的影响
DOI：
10.1557/jmr.2009.0031
复制
发表时间：
2009
影响因子：
2.7
通讯作者：
A. Inoue
中科院分区：
文献类型：
--
作者：
D. V. Louzguine;K. Georgarakis;A. Yavari;G. Vaughan;G. Xie;A. Inoue
利用实空间对分布和径向分布函数研究了Ag替代Cu对Cu_55Zr_45、Cu_45Zr_45Ag_10和Cu_35Zr_45Ag_20非晶合金结构特征的影响。在同步加速器光束中获得的实验X射线衍射数据通过傅里叶变换处理导出对和径向分布函数。这些结果表明，该合金中在约 2.5 nm 距离内保持一定程度的中程有序。研究表明，与二元 Cu-Zr 合金相比，Ag 的添加导致形成更均匀的局部原子结构，这可以被认为是该合金玻璃形成能力提高的原因。
The effect of Ag substituting Cu on the structural features of the Cu_55Zr_45, Cu_45Zr_45Ag_10, and Cu_35Zr_45Ag_20 glassy alloys was studied using the real-space pair distribution and radial distribution functions. The experimental x-ray diffraction data obtained in a synchrotron beam were used to derive pair and radial distribution functions through Fourier transformation processing. These results suggest that a certain degree of medium-range order in this alloy is maintained up to about 2.5 nm distance. It is suggested that the addition of Ag causes formation of a more homogeneous local atomic structure compared with that of a binary Cu–Zr alloy, which could be considered as a reason for the improved glass-forming ability of this alloy.
登录
查看更多内容
影响因子：
3.5
作者：
D. Louzguine;A. Yavari;K. Ota;G. Vaughan;A. Inoue
通讯作者：
D. Louzguine;A. Yavari;K. Ota;G. Vaughan;A. Inoue
二元和多组分体系中铜基大块非晶合金的合成和基本性能
DOI：
--
发表时间：
2004
期刊：
Mater. Trans. 45
影响因子：
--
作者：
Arma NR;Hirono I;Aoki T.;A. Inoue
通讯作者：
A. Inoue
DOI：
10.1016/j.msea.2007.02.039
发表时间：
2007-09
影响因子：
6.4
作者：
D. V. Louzguine-Luzgin;G. Xie;Wei Zhang;A. Inoue
通讯作者：
D. V. Louzguine-Luzgin;G. Xie;Wei Zhang;A. Inoue
影响因子：
4
作者：
D. V. Louzguine-Luzgin;A. Inoue;A. Yavari;G. Vaughan
通讯作者：
D. V. Louzguine-Luzgin;A. Inoue;A. Yavari;G. Vaughan
影响因子：
1.2
作者：
Takeuchi, A;Inoue, A
通讯作者：
Inoue, A