Synthesis and field emission of diamond-like carbon nanorods on TiO2/Ti nanotube arrays
Synthesis and field emission of diamond-like carbon nanorods on TiO2/Ti nanotube arrays
复制标题
TiO2/Ti 纳米管阵列上类金刚石碳纳米棒的合成及场发射
DOI：
10.1016/j.apsusc.2009.07.049
复制
发表时间：
2009-10
影响因子：
6.7
通讯作者：
J. Wang
中科院分区：
文献类型：
--
作者：
C. W. Wang;B. H. Ma;W. M. Liu;J. B. Chen;Y. Li;R. S. Guo;F. Zhou;J. Wang
在0.5wt%HF溶液中用阳极氧化法制备了高度有序的TiO{sub 2}/Ti纳米管阵列。以制备的TiO{sub 2}/Ti纳米管阵列为基体，采用化学气相沉积法在750 ℃下合成了高质量的类金刚石碳纳米棒（DLCNRs）。C在氮气气氛中。用场发射扫描电镜和拉曼光谱仪对DLCNRs进行了分析。有趣的是，DLCNRs呈宝塔状，长度为3-10 μ m.拉曼光谱在1332 cm{sup-1}和1598 cm{sup-1}处出现两个强峰，表明类金刚石碳的形成。场发射测试结果表明，DLCNRs/TiO 2/Ti具有良好的场发射性能，其开启场强约为3 0 V/μ m，在3 4 mA/cm 2下480 min内无明显衰减。
Highly ordered TiO{sub 2}/Ti nanotube arrays were fabricated by anodic oxidation method in 0.5 wt% HF. Using prepared TiO{sub 2}/Ti nanotube arrays deposited Ni nanoparticles as substrate, high quality diamond-like carbon nanorods (DLCNRs) were synthesized by a conventional method of chemical vapor deposition at 750 deg. C in nitrogen atmosphere. DLCNRs were analyzed by filed emission scanning electron microscopy and Raman spectrometer. It is very interesting that DLCNRs possess pagoda shape with the length of 3-10 {mu}m. Raman spectra show two strong peaks about 1332 cm{sup -1} and 1598 cm{sup -1}, indicating the formation of diamond-like carbon. The field emission measurements suggest that DLCNRs/TiO{sub 2}/Ti has excellent field emission properties, a low turn-on field about 3.0 V/{mu}m, no evident decay at 3.4 mA/cm{sup 2} in 480 min.
登录
查看更多内容
影响因子：
2.6
作者：
Woong Lee;M. Jeong;M. J. Kim;J. Myoung
通讯作者：
Woong Lee;M. Jeong;M. J. Kim;J. Myoung
影响因子：
3.5
作者：
M. Chen;K. Wu;J. Hwang;M. Chang;L. Chou;C. Kou
通讯作者：
M. Chen;K. Wu;J. Hwang;M. Chang;L. Chou;C. Kou
影响因子：
3.7
作者：
Arenal, R.;Bruno, P.;Gruen, D. M.
通讯作者：
Gruen, D. M.
影响因子：
3.5
作者：
Zhu, YW;Yu, T;Sow, CH
通讯作者：
Sow, CH
影响因子：
2.1
作者：
Da-yung Wang;Fengjin Chen;N. Wang;H. Yu
通讯作者：
Da-yung Wang;Fengjin Chen;N. Wang;H. Yu