Poling electric field dependent domain switching and piezoelectric properties of mechanically activated (Pb0.92La0.08)(Zr0.60Ti0.40)O3 ceramics
Poling electric field dependent domain switching and piezoelectric properties of mechanically activated (Pb0.92La0.08)(Zr0.60Ti0.40)O3 ceramics
复制标题
DOI：
10.1007/s10854-015-2899-1
复制
发表时间：
2015-06-01
影响因子：
2.8
通讯作者：
James, A. R.
中科院分区：
文献类型：
--
作者：
Kumar, Ajeet;Prasad, V. V. Bhanu;James, A. R.
(Pb0.92La0.08)(Zr0.60Ti0.40)O-3 (PLZT 8/60/40) ceramics were prepared via a combinatorial approach of high energy mechanical ball milling (mechanical activation), followed by cold isostatic pressing. Electrical properties of the piezoelectric ceramics are greatly influenced by the poling conditions (poling electric field, poling time and poling temperature). In this present study, the effect of the poling electric fields on the piezoelectric properties of PLZT 8/60/40 ceramics was investigated. It is a common practice to subject piezoelectric ceramics to electric fields well beyond their coercive fields, in order to pole them but here the measured values of piezoelectric (d(33) and g(33)) and electromechanical coupling coefficients (k(p), k(33) and k(31)) at different poling fields show that a ferroelectric material can be poled at similar to 5 kV/cm (< 0.5 E-c), far below the coercive field without compromising the induced high piezoelectricity. The results were discussed with the help of polarization, current and strain versus electric field curves.