Transition from internal to surface crack initiation of a single-crystal superalloy in the very-high-cycle fatigue regime at 1100 degrees C
Transition from internal to surface crack initiation of a single-crystal superalloy in the very-high-cycle fatigue regime at 1100 degrees C
复制标题
1100°C 超高周疲劳状态下单晶高温合金从内部裂纹萌生到表面裂纹萌生的转变
DOI：
10.1016/j.ijfatigue.2021.106343
复制
发表时间：
2021
影响因子：
6
通讯作者：
Chen B.
中科院分区：
文献类型：
--
作者：
Zhao Z.;Li Q.;Zhang F.;Xu W.;Chen B.