LiF/CaF2/LiBaF3 ternary fluoride eutectic scintillator
LiF/CaF2/LiBaF3 ternary fluoride eutectic scintillator
复制标题
LiF/CaF2/LiBaF3 三元氟化物共晶闪烁体
DOI：
10.7567/jjap.54.04dh04
复制
发表时间：
2015
影响因子：
1.5
通讯作者：
A. Yoshikawa
中科院分区：
文献类型：
--
作者：
Kosuke Hishinuma;K. Kamada;S. Kurosawa;A. Yamaji;J. Pejchal;Y. Yokota;Y. Ohashi;A. Yoshikawa
采用µ-PD法生长了LiF/CaF 2/LiBaF 3三元共晶晶体。在凝固的共晶中，各相沿横向均匀分布，并沿沿着排列。对于Eu掺杂的样品，在425 nm处观察到的预期发射峰归因于在X射线激发下Eu：CaF 2的Eu 2 + 5d-4f跃迁。LiF/CaF 2/LiBaF 3三元共晶晶体的光产额约为7，000光子/中子，衰减时间为260 ns（73.6%）和50 ns（26.4%）。
LiF/CaF2/LiBaF3 ternary eutectic scintillators were grown by the µ-PD method. In the solidified eutectic the phases were uniformly distributed in the transverse direction and aligned along the growth direction. For the Eu-doped samples, the expected emission peak observed at 425 nm was ascribed to Eu2+ 5d–4f transition from Eu:CaF2 under X-ray excitation. The LiF/CaF2/LiBaF3 ternary eutectic scintillators showed a light yield around 7,000 photons/neutron and decay time of 260 ns (73.6%) and 50 ns (26.4%).
估算三元共晶体系有序和晶格参数的新金相方法
DOI：
10.1007/s13632-013-0072-x
发表时间：
2013
期刊：
Metallography, Microstructure, and Analysis
影响因子：
--
作者：
A. Dennstedt;L. Ratke;A. Choudhury;B. Nestler
通讯作者：
B. Nestler