Corrosion in high alumina refractory serviced in a bench-scale entrained flow gasifier
Corrosion in high alumina refractory serviced in a bench-scale entrained flow gasifier
复制标题
小型气流床气化炉中使用的高铝耐火材料的腐蚀
DOI：
10.1016/j.ceramint.2020.09.061
复制
发表时间：
2021-01
影响因子：
5.2
通讯作者：
Guangsuo Yu
中科院分区：
文献类型：
--
作者：
Shuai Wang;Qinghua Guo;Yan Gong;Shuhong Liao;Lingling Bao;Guangsuo Yu
Corroded microstructure of high alumina refractory serviced in a bench-scale entrained flow gasifier was investigated. The bench-scale gasifier established a relatively real environment: 0.1 MPa, 1400–1450 °C and reducing atmosphere. By analyzing the two stages of the slag accumulation and slag further corrosion in pore structures, it was found that the refractory in the pore structures was dissolved and formed low temperature eutectics with the slag penetrating. Moreover, the compositions of the slag infiltrated around the burner plane was compared and the results indicated that the slag infiltrated into the refractory above the burner plane had a higher solubility to the refractory. Thermodynamic equilibrium calculation for the mixture of refractory and slag was used to predict the changes of solid phase and liquid phase. Additionally, as the slag penetrated and the temperature decreased, anorthite (Ca2Al2Si2O8) was the first to precipitate.
登录
查看更多内容
微孔氧化铝与各种CaO-Al2O3-SiO2渣接触的隔离或腐蚀
影响因子：
8.3
作者：
Fu Lvping;Huang Ao;Lian Pengfei;Gu Huazhi
通讯作者：
Gu Huazhi
影响因子：
5.7
作者：
M. Carlborg;F. Weiland;Charlie Ma;R. Backman;I. Landälv;H. Wiinikka
通讯作者：
M. Carlborg;F. Weiland;Charlie Ma;R. Backman;I. Landälv;H. Wiinikka
影响因子：
3.9
作者：
T. Kaneko;Jingxi Zhu;H. Thomas;J. Bennett;S. Sridhar
通讯作者：
T. Kaneko;Jingxi Zhu;H. Thomas;J. Bennett;S. Sridhar
影响因子：
5.7
作者：
Guo, Qinghua;Zhang, Zhiqing;Wang, Fuchen
通讯作者：
Wang, Fuchen
Cr2O3添加量对垃圾熔炉用耐火浇注料腐蚀机理及六价铬并发生成的影响
影响因子：
5.2
作者：
Nath, Mithun;Song, Shengqiang;Xu, Yibiao
通讯作者：
Xu, Yibiao