Dy(9.33-x)Lax(SiO4)6O2 crystals with improved magneto-optical performances prepared by Czochralski growth method
Dy(9.33-x)Lax(SiO4)6O2 crystals with improved magneto-optical performances prepared by Czochralski growth method
复制标题
直拉生长法制备具有改善磁光性能的 Dy(9.33-x)Lax(SiO4)6O2 晶体
DOI：
10.1016/j.optmat.2020.109868
复制
发表时间：
2020-07
影响因子：
3.9
通讯作者：
Jianzhong Chen
中科院分区：
文献类型：
--
作者：
Xin Chen;Mingzhen Du;Li Dai;Cheng Chang;Xiaolin Hu;Feiyun Guo;Naifeng Zhuang;Jianzhong Chen
本文采用提拉法生长了Dy（9.33-x）Lax（SiO 4）6 O2晶体，并对其磁光性能进行了研究。Rietveld结构精修的XRD图谱表明Dy（9.33-x）Lax（SiO 4）6 O2具有六方晶系P63/m的氧磷灰石结构。UV-Vis-NIR光谱显示，与PSO和TGG晶体相比，在420-700 nm光谱区域具有更高的透明度。磁光性质和磁化率的温度依赖性表明，Dy 8.36 La 0.97（SiO 4）6 O2晶体在2-300 K温度范围内表现出顺磁行为，产生的法拉第旋转角约为Tb 3Ga 5 O 12晶体的1.16倍。总的来说，Dy8.36La0.97（SiO 4）6 O2晶体在可见光波段磁光器件中具有良好的应用前景。
In this account, Dy(9.33-x)Lax(SiO4)6O2crystals were grown by the Czochralski technique, and their magneto-optical properties were examined. Rietveld structural refinement of XRD patterns illustrated Dy(9.33-x)Lax(SiO4)6O2possess hexagonal systemP63/m with oxyapatite structure. UV–Vis–NIR spectroscopy revealed higher transparency in the 420–700 nm spectral region when compared to PSO and TGG crystals. The magneto-optical properties and temperature dependence of magnetic susceptibility demonstrate that Dy8.36La0.97(SiO4)6O2crystals show paramagnetic behavior within the temperature range of 2–300 K and yield a Faraday rotation angle which is approximately 1.16-fold larger than that of Tb3Ga5O12crystals. Overall, Dy8.36La0.97(SiO4)6O2crystals look promising for applications in magneto-optical devices in the visible wavelength range.
登录
查看更多内容
影响因子：
3.5
作者：
O. El-Bayoumi;M. Drexhage;A. J. Bruce;J. Schroeder;C. T. Moynihan
通讯作者：
O. El-Bayoumi;M. Drexhage;A. J. Bruce;J. Schroeder;C. T. Moynihan
影响因子：
3.8
作者：
K. Shimamura;T. Kito;E. Castel;A. Latynina;P. Molina;E. Vı́llora;P. Mythili;P. Veber;J. Chaminad
通讯作者：
K. Shimamura;T. Kito;E. Castel;A. Latynina;P. Molina;E. Vı́llora;P. Mythili;P. Veber;J. Chaminad
影响因子：
4
作者：
S. Kahl;A. Grishin
通讯作者：
S. Kahl;A. Grishin
影响因子：
3.2
作者：
S. Rosenkranz;A. P. Ramirez;A. Hayashi;R. Cava;R. Siddharthan;B. Shastry
通讯作者：
S. Rosenkranz;A. P. Ramirez;A. Hayashi;R. Cava;R. Siddharthan;B. Shastry
影响因子：
--
作者：
J. V. Vleck;M. H. Hebb
通讯作者：
J. V. Vleck;M. H. Hebb