Reaction layer at the interface between aluminium particles and a glass substrate formed by cold spray
Reaction layer at the interface between aluminium particles and a glass substrate formed by cold spray
复制标题
冷喷涂形成的铝颗粒与玻璃基板界面反应层
DOI：
10.1088/0022-3727/46/19/195301
复制
发表时间：
2013
期刊：
影响因子：
--
通讯作者：
Seiji Kuroda and Kazuhiko Sakaki
中科院分区：
文献类型：
--
作者：
Minghui Song;Hiroshi Araki;Seiji Kuroda and Kazuhiko Sakaki
一个低密度的界面层的厚度可达80 nm的发现和其特征在于在冷喷涂Al颗粒和钠钙玻璃基板之间的界面处的透射电子显微镜。该层由非晶和纳米晶粒组成，并且具有与Al和玻璃不同的化学成分。据认为，该层是由喷涂的Al与玻璃的反应产生的，并且它充当它们之间的结合层。
A low-density interface layer of thickness up to 80 nm was found and characterized at the interface between cold-sprayed Al particles and a soda-lime glass substrate with transmission electron microscopy. The layer was composed of amorphous and nano-crystalline grains, and had a different chemical composition from Al and glass. It is suggested that the layer resulted from the reaction of the sprayed Al with glass, and that it acted as a bonding layer between them.