On the mechanism of very high cycle fatigue in Ti-6Al-4V
On the mechanism of very high cycle fatigue in Ti-6Al-4V
复制标题
DOI：
10.1016/j.scriptamat.2008.08.012
复制
发表时间：
2008-12
影响因子：
6
通讯作者：
A. J. Mcevily;Takashi Nakamura;H. Oguma;K. Yamashita;H. Matsunaga;M. Endo
中科院分区：
文献类型：
--
作者：
A. J. Mcevily;Takashi Nakamura;H. Oguma;K. Yamashita;H. Matsunaga;M. Endo
提出了Ti-6Al-4V材料的高周疲劳机制，其中包括真空中裂纹闭合的侵蚀。
A mechanism of fatigue crack advance involving the erosion of crack closure in vacuum is proposed to account for the very high cycle fatigue of Ti–6Al–4V.