Fracture toughness of China low activation martensitic (CLAM) steel at room temperature
Fracture toughness of China low activation martensitic (CLAM) steel at room temperature
复制标题
中国低活化马氏体（CLAM）钢的室温断裂韧性
DOI：
10.1016/j.fusengdes.2014.03.076
复制
发表时间：
2014-04
影响因子：
1.7
通讯作者：
Siben Jiang
中科院分区：
文献类型：
--
作者：
Kunfeng Li;Shaojun Liu;Qunying Huang;Gang Xu;Siben Jiang
用紧凑型拉伸试验机测试了中国低活性马氏体钢的室温断裂韧性，结果为417.9 kJ/m2，与同等条件下的断裂韧性JLf-1相近。断口显微组织观察表明，断裂方式为典型的韧性断裂。同时，还利用分维计算了材料的断裂韧性，计算结果为454.6 kJ/m2，与实验结果吻合较好。该方法可以通过对断口的分析来估算材料的断裂韧度。
The fracture toughness (JIC) of China low activation martensitic (CLAM) steel was tested at room temperature through the compact tension specimen, the result is 417.9 kJ/m2, which is similar to the JLF-1 at same experimental conditions. The microstructural observation of the fracture surface shows that the fracture mode is a typical ductile fracture. Meanwhile, the fracture toughness is also calculated on the basis of the fractal dimension and the calculated result is 454.6 kJ/m2, which is consistent well with the experimental result. This method could be used to estimate the fracture toughness of materials by analyzing of the fracture surface.
登录
查看更多内容
影响因子：
3.1
作者：
M. Sokolov;A. Kimura;H. Tanigawa;S. Jitsukawa
通讯作者：
M. Sokolov;A. Kimura;H. Tanigawa;S. Jitsukawa
DOI：
10.3390/ma5050922
发表时间：
2012-05-23
期刊：
Materials (Basel, Switzerland)
影响因子：
--
作者：
Pramanik B;Tadepalli T;Mantena PR
通讯作者：
Mantena PR
影响因子：
0.9
作者：
L. Heung;H. Sessions;Xuesu Xiao;H. Mentzer
通讯作者：
L. Heung;H. Sessions;Xuesu Xiao;H. Mentzer
DOI：
10.1520/stp725-eb
发表时间：
1981
期刊：
--
影响因子：
--
作者：
M. Grossbeck;T. Allen;R. Lott;Arvind S. Kumar
通讯作者：
M. Grossbeck;T. Allen;R. Lott;Arvind S. Kumar
DOI：
10.1016/j.fusengdes.2008.12.037
发表时间：
2009-06
期刊：
--
影响因子：
--
作者：
Shaojun Liu;Qunying Huang;Chunjing Li;B. Huang
通讯作者：
Shaojun Liu;Qunying Huang;Chunjing Li;B. Huang