X-ray tomographic observation of environmental assisted cracking in heat-treated lean duplex stainless steel
X-ray tomographic observation of environmental assisted cracking in heat-treated lean duplex stainless steel
复制标题
热处理贫双相不锈钢环境辅助开裂的 X 射线断层扫描观察
DOI：
10.1016/j.corsci.2021.109363
复制
发表时间：
2021
影响因子：
8.3
通讯作者：
Eguchi K
中科院分区：
文献类型：
--
作者：
Eguchi K
通过X射线计算机断层扫描（X-ray CT）和截面显微组织分析，观察到热处理后贫双相不锈钢发生环境辅助开裂（EAC）。铁素体相的选择性腐蚀发生在样品表面，与内部腐蚀所施加的塑性应变触发。观察到的裂纹主要沿沿着铁素体-铁素体晶界扩展，裂纹止裂与铁素体-奥氏体晶界有关。EAC断裂过程中的裂纹扩展进行了观察，在operando。EAC的突然出现是由于韧性奥氏体相对裂纹张开的抑制。降低EAC电阻归因于氢脆效应。
The occurrence of environmental assisted cracking (EAC) has been observed in heat-treated lean duplex stainless steel via X-ray computed tomography (X-ray CT) and cross-sectional microstructure analysis. Selective corrosion of the ferrite phase occurred at the sample surface, with internal corrosion triggered by applied plastic strain. The observed cracks mainly propagated along ferrite-ferrite boundaries, with crack arrest associated with ferrite-austenite grain boundaries. Crack propagation during EAC fracture was observed, in-operando. The sudden appearance of EAC occurred due to the suppression of crack opening by ductile austenite phase. The reduced EAC resistance was attributed to hydrogen embrittlement effects.
登录
查看更多内容
通过组合亚微米 EBSD 和 EPMA 碳测量表征双相钢微观结构
影响因子：
2.8
作者：
A. Schwedt;A. Ramazani;U.Prahl;S. Richter
通讯作者：
S. Richter
精益双相材料 UNS S32202 的耐腐蚀性能
DOI：
--
发表时间：
2015
期刊：
影响因子：
--
作者：
S. Manchet;B. Chareyre;E. Chauveau;N. Bouvier;T. Mesquita
通讯作者：
T. Mesquita
冷加工对302型奥氏体不锈钢应力腐蚀裂纹的影响
DOI：
--
发表时间：
1965
期刊：
影响因子：
--
作者：
P. J. Greeley;V. J. Russo;R. Saxer;J. Myers
通讯作者：
J. Myers
精益双相不锈钢的去钝化机理及合金元素分配的影响
DOI：
--
发表时间：
2014
期刊：
影响因子：
--
作者：
F. Ruel;D. Tite;A. Gaugain;S. Saedlou;K. Wolski
通讯作者：
K. Wolski
DOI：
10.1007/s11661-009-0050-8
发表时间：
2009-12-01
影响因子：
2.8
作者：
Saeed-Akbari, A.;Imlau, J.;Bleck, W.
通讯作者：
Bleck, W.