Photopolymerized C60 Film by XPS
复制标题
XPS 光聚合 C60 薄膜
DOI：
10.1116/1.1247876
复制
发表时间：
1998
影响因子：
1.3
通讯作者：
K. Takeuchi
中科院分区：
文献类型：
--
作者：
A. Nakao;J. Onoe;K. Takeuchi
我们在这里提出的变化的价带和C 1 s核心峰和它的震动卫星的C60膜光聚合后，使用X射线光电子能谱。结果表明，随着500 W汞灯照射时间的延长（0 ~ 200 h），光转化膜的C1 s震荡卫星强度逐渐降低。另一方面，价带光谱的C60膜几乎没有变化，即使在200小时的照射后，与原始的C60膜相比。
We present here the changes in the valence band and the C 1s core peak and its shake-up satellite of a C60 film upon photopolymerization using x-ray photoelectron spectroscopy. It was found that the intensity of the C 1s shake-up satellite of the phototransformed C60 film decreased with increasing irradiation time of 500 W mercury lamp (0 to 200 h). On the other hand, the valence band spectra of the C60 film was almost unchanged even after 200 h of irradiation, compared with that of pristine C60 film.