Characterization of the Microstructure after Composite Peening of Aluminum
Characterization of the Microstructure after Composite Peening of Aluminum
复制标题
铝复合喷丸后的显微组织表征
DOI：
10.1002/adem.202000575
复制
发表时间：
2020
影响因子：
3.6
通讯作者：
Weidenmann
中科院分区：
文献类型：
--
作者：
Dürrschnabel;Kauffmann;Kurpiers;Greiner;Weidenmann
复合喷丸是将陶瓷喷丸颗粒引入基体表面的一种新型工艺。根据工艺参数的不同，爆破颗粒的穿透深度可达几微米。在一些作者之前的研究中发现，在复合强化过程中加入的陶瓷颗粒比强化前的10 μm尺寸要小得多。重点介绍了复合强化后的微观组织。为了研究这种微观结构，进行了扫描电子显微镜（SEM）和透射电子显微镜（TEM）。随后的X射线衍射（XRD）分析进一步证明了由破碎的爆破颗粒组成的严重变形的纳米晶陶瓷层。
Composite peening is a novel process to introduce ceramic blasting particles into the surface of substrates. Depending on the process parameters, the penetration depth of the blasting particles can be several micrometers. In previous investigations by some of the authors, it has been found that the ceramic particles incorporated during composite peening are significantly smaller compared to 10 μm in size before peening. Herein, the microstructure after composite peening is highlighted. To investigate this microstructure, scanning electron microscopy (SEM) and transmission electron microscopy (TEM) are performed. The subsequent X‐ray diffraction (XRD) analysis provides further evidence of a severely deformed, nanocrystalline ceramic layer consisting of fragmented blasting particles.
登录
查看更多内容
复合喷丸——梯度增强铝基复合材料的新型加工技术
DOI：
10.4028/www.scientific.net/kem.742.137
发表时间：
2017
期刊：
Key Engineering Materials
影响因子：
--
作者：
Klumpp;Weidenmann
通讯作者：
Weidenmann
Haynes Stellite 6B I 中颗粒侵蚀损伤的研究：侵蚀表面的扫描电子显微镜
影响因子：
5
作者：
J. W. Edington;I. Wright
通讯作者：
I. Wright
正常冲击下固体球形颗粒对铝合金侵蚀的关键研究
影响因子：
5
作者：
A. Cousens;I. Hutchings
通讯作者：
I. Hutchings
现代伦琴博古
DOI：
--
发表时间：
2019
期刊：
影响因子：
--
作者：
L. Spieß;G. Teichert;R. Schwarzer;H. Behnken;C. Genzel
通讯作者：
C. Genzel
影响因子：
4.5
作者：
LEWIS, D;WHEELER, EJ
通讯作者：
WHEELER, EJ