Threshold for Stress Corrosion Cracking Initiation of Alloy X750 under Long-Term Uniaxial Constant Load Test in High-Temperature Water
Threshold for Stress Corrosion Cracking Initiation of Alloy X750 under Long-Term Uniaxial Constant Load Test in High-Temperature Water
复制标题
X750合金高温水中长期单轴恒载荷试验应力腐蚀开裂阈值
作者：
M. Yamamoto;J. Kuniya;S. Uchida
摘要对镍基合金X750（UNS N07550）在高温纯水（288°C，8 ppm溶解氧[DO]）中进行了单轴恒载荷（UCL）试验，以研究其应力腐蚀行为。
Abstract Uniaxial constant load (UCL) tests of the nickel-based alloy X750 (UNS N07550) were performed in high-temperature pure water (288°C, 8 ppm dissolved oxygen [DO]) to investigate stress corr...