Preparation of porous nanoparticle TiO2 films for flexible dye-sensitized solar cells
Preparation of porous nanoparticle TiO2 films for flexible dye-sensitized solar cells
复制标题
柔性染料敏化太阳能电池用多孔纳米TiO2薄膜的制备
DOI：
10.1007/s11434-011-4532-x
复制
发表时间：
2011-08
影响因子：
--
通讯作者：
Huang MiaoLiang
中科院分区：
文献类型：
--
作者：
Wang Yue;Wu JiHuai;Lan Zhang;Xiao YaoMing;Li QingBei;Peng FuGuo;Lin JianMing;Huang MiaoLiang
A TiO2 paste was prepared by mixing commercial TiO2 (P25), ethanol, distilled water and a small amount of Ti (IV) tetraisopropoxide (TTIP), following by a hydrothermal treatment. Before hydrothermal treatment, a stirring for 48 h can prevent cracking TiO2 films. TTIP significantly promote the chemical connection between TiO2 particles and its adherence to the substrate, the TTIP amount of 6 mol% is suitable. UV irradiation can remove some impurities and water from the TiO2 film with an optimal time of 2 h. Transmission electron microscopy, X-ray diffraction, scanning electron microscopy and photovoltaic tests are characterized and measured. Short-circuit current density, open-circuit voltage, fill factor and photoelectric conversion efficiencies for the fabricated flexible dye-sensitized solar cell are 7.20 mA cm−2, 0.769 V, 0.686 and 3.84%, respectively, under irradiation with a simulated solar light of 100 mW cm−2.
登录
查看更多内容
DOI：
10.1016/s1010-6030(03)00106-0
发表时间：
2003-06
影响因子：
4.3
作者：
Claudia Longo;J. Freitas;M. Paoli
通讯作者：
Claudia Longo;J. Freitas;M. Paoli
DOI：
10.1016/j.jphotochem.2003.11.021
发表时间：
2004-06
影响因子：
4.3
作者：
T. Murakami;Yujiro Kijitori;N. Kawashima;T. Miyasaka
通讯作者：
T. Murakami;Yujiro Kijitori;N. Kawashima;T. Miyasaka
影响因子：
--
作者：
李成玉
通讯作者：
李成玉
影响因子：
5.4
作者：
Li Yang;Liqiong Wu;Mingxing Wu;G. Xin;Hong Lin;T. Ma
通讯作者：
Li Yang;Liqiong Wu;Mingxing Wu;G. Xin;Hong Lin;T. Ma
影响因子：
4.6
作者：
Grätzel, M
通讯作者：
Grätzel, M