Giant magnetocaloric and magnetoresistance effects in ferrimagnetic Mn1.9Co0.1Sb alloy
Giant magnetocaloric and magnetoresistance effects in ferrimagnetic Mn1.9Co0.1Sb alloy
复制标题
亚铁磁性Mn1.9Co0.1Sb合金的巨磁热效应和磁阻效应
DOI：
10.1063/1.4862332
复制
发表时间：
2014-01
影响因子：
4
通讯作者：
Y. W. Du
中科院分区：
文献类型：
--
作者：
Y. L. Huang;Z. C. Zhong;D. H. Wang;Y. W. Du
研究了Mn1.9Co0.1Sb金属间化合物的磁性和相变行为。Mn_2Sb是一种简单的亚铁磁体，其Neel温度约为550 K。Co的引入导致了Mn 1.9Co 0.1Sb合金中反铁磁态的出现，从而在反铁磁态和亚铁磁态之间发生了一级磁转变，这种转变可以由温度/磁场诱导实现。相应地，在10和50 kOe的场变化下分别实现了高达5 J kg-1 K-1的磁熵变和46%的大磁阻。
Magnetic and transitional behaviors are investigated in Mn1.9Co0.1Sb intermetallic compound. Mn2Sb is a simple ferrimagnet with Neel temperature around 550 K. The Co-introduction results in the appearance of antiferromagnetic state, and therefore, the first-order magnetic transition occurs between antiferromagnetic and ferrimagnetic state, which can be induced by temperature/magnetic field, in Mn1.9Co0.1Sb alloy. Accordingly, a magnetic entropy change as high as 5 J kg−1 K−1 and a large magnetoresistance of 46% under the field change of 10 and 50 kOe are achieved, respectively.
登录
查看更多内容
影响因子：
4
作者：
Jian Liu;N. Scheerbaum;J. Lyubina;O. Gutfleisch
通讯作者：
Jian Liu;N. Scheerbaum;J. Lyubina;O. Gutfleisch
影响因子：
6.2
作者：
Y. Nagata;Toshiharu Hagii;S. Yashiro;H. Samata;S. Abe
通讯作者：
Y. Nagata;Toshiharu Hagii;S. Yashiro;H. Samata;S. Abe
影响因子：
2.7
作者：
M. Ohashi;Y. Yamaguchi;T. Kanomata
通讯作者：
M. Ohashi;Y. Yamaguchi;T. Kanomata
影响因子：
0.6
作者：
V. M. Ryzhkovskii;V. Glazkov;V. S. Goncharov;D. Kozlenko;B. Savenko
通讯作者：
V. M. Ryzhkovskii;V. Glazkov;V. S. Goncharov;D. Kozlenko;B. Savenko
DOI：
10.1016/0031-9163(64)91158-8
发表时间：
1964-01-01
期刊：
PHYSICS LETTERS
影响因子：
--
作者：
BANERJEE, SK
通讯作者：
BANERJEE, SK