Effect of surface roughness of Chinese sub-bituminous coal on the kinetics of three-phase contact formation
Effect of surface roughness of Chinese sub-bituminous coal on the kinetics of three-phase contact formation
复制标题
中国次烟煤表面粗糙度对三相接触形成动力学的影响
DOI：
10.1016/j.fuel.2017.12.053
复制
发表时间：
2018-03
期刊：
影响因子：
7.4
通讯作者：
Tao Xiuxiang
中科院分区：
文献类型：
--
作者：
Wang Shiwei;Guo Jifeng;Tang Longfei;He Huan;Tao Xiuxiang
本文研究了不同表面粗糙度的低阶煤表面三相接触线（TPC）的末端直径和扩展速度。为了消除低阶煤颗粒亲水表面的不均匀性影响，采用低灰分含量的实验样品。此外，XPS分析结果表明，低阶煤表面亲水矿物颗粒很少。此外，从SEM和AFM测量分析可以看出，低阶煤表面的不同局部区域存在许多不同尺寸（高度和宽度）的缝隙（柱子、突起）。因此，低阶煤表面的三相接触线呈现出不同的润湿行为。结果表明，低阶煤样表面粗糙度增大，润湿膜直径变小，三相接触线扩展速度加快。
In this paper, terminal diameter and expansion velocity of the three-phase contact (TPC) line on the low-rank coal surfaces with different surface roughness were investigated. To eliminate the heterogeneity effect on the hydrophilic surfaces of low-rank coal particles, experimental samples with low ash content were adopted. Moreover, the analysis result of XPS indicated that there were few hydrophilic mineral particles on the low-rank coal surface. Furthermore, from the analyses of SEM and AFM measurements there are many crevices (pillars, protrusions) of different sizes (height and width) in different local areas of low-rank coal surfaces. Therefore, the three-phase contact lines on the low-rank coal surfaces presented different wetting behaviors. It demonstrated that the wetting film diameter became smaller and the expansion velocity of the three-phase contact line was faster while the surface roughness of low-rank coal samples increased.
登录
查看更多内容
影响因子：
4.8
作者：
Anh V. Nguyen;L. Alexandrova;L. Grigorov;G. Jameson
通讯作者：
Anh V. Nguyen;L. Alexandrova;L. Grigorov;G. Jameson
DOI：
--
发表时间：
1991-08
期刊：
--
影响因子：
--
作者：
C. Tanford
通讯作者：
C. Tanford
影响因子：
--
作者：
Anh V. Nguyen;H. Schulze;J. Ralston
通讯作者：
Anh V. Nguyen;H. Schulze;J. Ralston
影响因子：
--
作者：
J. Zawała;J. Drzymała;K. Małysa
通讯作者：
J. Zawała;J. Drzymała;K. Małysa
DOI：
10.1039/c2cp43545d
发表时间：
2013-01
期刊：
Physical chemistry chemical physics : PCCP
影响因子：
--
作者：
D. Kosior;J. Zawała;M. Krasowska;K. Małysa
通讯作者：
D. Kosior;J. Zawała;M. Krasowska;K. Małysa