Growth and properties of TSAG and TSLAG magneto-optical crystals with large size
Growth and properties of TSAG and TSLAG magneto-optical crystals with large size
复制标题
大尺寸TSAG和TSLAG磁光晶体的生长及性能
DOI：
10.1016/j.optmat.2019.109272
复制
发表时间：
2019-10
影响因子：
3.9
通讯作者：
Sun Dunlu
中科院分区：
文献类型：
--
作者：
Dou Renqin;Zhang Haotian;Zhang Qingli;Zhuang Naifeng;Liu Wenpeng;He Yi;Chen Yingying;Cheng Maojie;Luo Jianqiao;Sun Dunlu
用提拉法成功地生长出了尺寸为65 mm × 70 mm的大尺寸高透明TSAG和TSLAG单晶。TSAG和TSLAG在473、532、632.8和1064 nm处的折射率分别为1.9214 - 1.8817和1.9242 - 1.8841。他们的Sellmeier方程拟合。测量了TSAG和TSLAG在300 - 373 K、300 - 473 K、300 - 573 K、300 - 673 K和300 - 773 K的平均热膨胀系数。TSAG和TLSAG晶体的热膨胀系数值在测量误差范围内（相差0.3-0.4%）一致。TSAG和TSLAG的热扩散率值在300 K时分别为1.454和1.418 mm 2s − 1。根据比热计算结果，TSAG和TSLAG在300 K时的热导率分别为4.45和4.20 W（m K）− 1。此外，TSAG在532、633和1064 nm处的费尔德常数分别为218、152和65 rad/m/T，而TSLAG的费尔德常数分别为246、146和56 rad/m/T。进一步得到了TSAG和TSLAG的费尔德常数与波长的关系。
Large size high transparent TSAG and TSLAG single crystals of Ø 65 mm × 70 mm have been grown successfully by the Cz method. The refractive indices at 473, 532, 632.8 and 1064 nm are 1.9214 - 1.8817 for TSAG and 1.9242 - 1.8841 for TSLAG. Their Sellmeier equations are fitted. The average thermal expansion coefficients of TSAG and TSLAG at 300 – 373 K, 300 – 473 K, 300 – 573 K, 300 – 673 K, and 300 – 773 K are measured. The values of thermal expansion coefficients of TSAG and TLSAG crystals coincide within the measurement error (differ by 0.3–0.4%). The thermal diffusivity values of TSAG and TSLAG are 1.454 and 1.418 mm2s−1at 300 K, respectively. Calculated with the specific heat results, the values of thermal conductivity of TSAG and TSLAG are 4.45 and 4.20 W (m K)−1at 300 K. Moreover, the Verdet constants of TSAG are 218, 152, and 65 rad/m/T at 532, 633, and 1064 nm, while those of TSLAG are 246, 146, and 56 rad/m/T, respectively. In further, the relationships between Verdet constant and wavelength of TSAG and TSLAG are obtained.
登录
查看更多内容
影响因子：
3.2
作者：
C. B. Rubinstein;L. G. Uitert;W. H. Grodkiewicz
通讯作者：
C. B. Rubinstein;L. G. Uitert;W. H. Grodkiewicz
影响因子：
3.9
作者：
F. Guo;Xin Chen;Zhongliang Gong;Xiang Chen;Bin Zhao;Jianzhong Chen
通讯作者：
F. Guo;Xin Chen;Zhongliang Gong;Xiang Chen;Bin Zhao;Jianzhong Chen
影响因子：
3.1
作者：
R. Dou;Qingli Zhang;D. Sun;Jianqiao Luo;Huajun Yang;Wenpeng Liu;Guihua Sun
通讯作者：
R. Dou;Qingli Zhang;D. Sun;Jianqiao Luo;Huajun Yang;Wenpeng Liu;Guihua Sun
影响因子：
3.8
作者：
K. Shimamura;T. Kito;E. Castel;A. Latynina;P. Molina;E. Vı́llora;P. Mythili;P. Veber;J. Chaminad
通讯作者：
K. Shimamura;T. Kito;E. Castel;A. Latynina;P. Molina;E. Vı́llora;P. Mythili;P. Veber;J. Chaminad
影响因子：
3.6
作者：
D. Gauthier;P. Narum;R. Boyd
通讯作者：
D. Gauthier;P. Narum;R. Boyd