在还原气氛下制备了30 CaF 2 - 10Al 2 O3 - 60 B2 O3（mol%）和30 CaO-10Al 2 O3 - 60 B2 O3（mol%）的掺Eu 3+氟氧化物玻璃。在10 ~ 300 K温度范围内，研究了Eu 3+掺杂玻璃基质30 CaF 2 -10Al 2 O3 - 60 B2 O3和30 CaO-10Al 2 O3 - 60 B2 O3的持续光谱烧孔（PSHB）现象，并比较了它们的烧孔效率。
Eu 3+ -doped oxyfluoride glasses with composition of 30C a F 2 -10Al 2 O 3 -60B 2 O 3 (mol%) and oxide glasses of 30CaO-10Al 2 O 3 -60B 2 O 3 (mol%) were prepared in a reducing atmosphere. The persistent spectral hole burning (PSHB) was characterized over a temperature range from 10 to 300 K, and the hole-burning efficiency between Eu 3+ -doped glass matrix of 30CaF2-10Al 2 O 3 -60B 2 O 3 and 30CaO-10Al 2 O 3 -60B 2 O 3 was compared.