Discontinuous oxidation and erosion-oxidation of a CeO2-dispersion-strengthened chromium coating
Discontinuous oxidation and erosion-oxidation of a CeO2-dispersion-strengthened chromium coating
复制标题
CeO2 弥散强化铬涂层的不连续氧化和侵蚀氧化
DOI：
10.1016/j.corsci.2010.02.009
复制
发表时间：
2010-05
影响因子：
8.3
通讯作者：
Xu C
中科院分区：
文献类型：
--
作者：
Peng X;Wang F;Dong Z;Yan J;Xu C
采用两步法在碳钢表面制备了CeO 2弥散强化铬镀层：先电沉积Ni-CeO 2纳米复合镀层，然后采用传统的固体渗铬方法进行渗铬。与在碳钢上制备的无CeO 2涂层相比，在900°C下，在5%O2 + N2和5%O2 + 1000 ppm SO2+N2中，CeO 2分散的铬涂层提供了显著改善的抗不连续氧化性，以及在实验室规模的流化床燃烧器（FBC）中的抗侵蚀-氧化性，主要是因为开发了致密的，皱纹较少且粘附性更强的氧化铬鳞。
A CeO2-dispersion-strengthened chromium coating was developed on a carbon steel using a two-step process: prior electrodeposition of a Ni-CeO2nanocomposite film and subsequent chromization using a conventional pack cementation method. Compared to the CeO2-free coatings prepared on the carbon steel without and with pre-electrodeposition of a pure Ni film, the CeO2dispersed chromium coating offered profoundly improved discontinuous oxidation resistance at 900°C in 5% O2+N2and in 5% O2+1000ppm SO2+N2, and erosion-oxidation resistance in a laboratory-scale fluidized-bed combustor (FBC), mainly because of the development of a denser, less wrinkled and more adherent chromia scale.
登录
查看更多内容
影响因子：
2.2
作者：
A. Evans;G. B. Crumley;R. E. Demaray
通讯作者：
A. Evans;G. B. Crumley;R. E. Demaray
影响因子：
5.4
作者：
Jyh-Wei Lee;J. Duh
通讯作者：
Jyh-Wei Lee;J. Duh
影响因子：
2.2
作者：
GOLIGHTLY, FA;STOTT, FH;WOOD, GC
通讯作者：
WOOD, GC
DOI：
10.1039/b815907f
发表时间：
2009-02
期刊：
Physical chemistry chemical physics : PCCP
影响因子：
--
作者：
S. Benny;R. Grau‐Crespo;N. D. de Leeuw
通讯作者：
S. Benny;R. Grau‐Crespo;N. D. de Leeuw
影响因子：
9.4
作者：
R. Christensen;D. M. Lipkin;D. Clarke
通讯作者：
R. Christensen;D. M. Lipkin;D. Clarke