Assessment of the impact of hydrogen on the stress developed ahead of a fatigue crack
Assessment of the impact of hydrogen on the stress developed ahead of a fatigue crack
复制标题
DOI：
10.1016/j.actamat.2019.05.028
复制
发表时间：
2019-08
期刊：
影响因子：
9.4
通讯作者：
Shuai Wang;A. Nagao;P. Sofronis;I. Robertson
中科院分区：
文献类型：
--
作者：
Shuai Wang;A. Nagao;P. Sofronis;I. Robertson
The microstructure generated in a low carbon steel under cyclic loading in air and a 40 MPa gaseous hydrogen environment has been compared as a function of distance from the crack tip. The presence of hydrogen resulted in the formation of a smaller and more equiaxed dislocation cell structure that extended further from the crack tip than the one generated in air. This enhancement and extension of the dislocation structure by hydrogen is consistent with it modifying the generation rate and mobility of dislocations as well as dislocation interactions. Qualitative assessment of the dislocation structure ahead of the crack tip found the stress ahead of the crack tip to vary linearly as ln(1/x), wherexis the distance from the crack tip irrespective of the test environment. Hydrogen caused a shift to higher stresses, implying the critical damage level for crack propagation will be achieved more rapidly with a concomitant increase in the crack propagation rate.