Fabrication of a hierarchical trimodal structure with nano-cellular Cu2O, nano-porous Cu and micro-porous Gasar Cu
Fabrication of a hierarchical trimodal structure with nano-cellular Cu2O, nano-porous Cu and micro-porous Gasar Cu
复制标题
纳米多孔 Cu2O、纳米多孔 Cu 和微孔 Gasar Cu 分级三峰结构的制备
DOI：
10.1016/j.matlet.2015.11.024
复制
发表时间：
2016-02
影响因子：
3
通讯作者：
Y. Cheng
中科院分区：
文献类型：
--
作者：
M. Du;H. W. Zhang;Y. X. Li;Y. Liu;X. Chen;Y. He;Y. Cheng
通过在Gasar孔内表面熔覆Cu - zn合金层，通过自发氧化法制备了微孔Gasar Cu、纳米孔Gasar Cu和纳米胞状氧化亚铜（Cu2O）的分层三峰结构。研究了腐蚀时间对纳米多孔Cu和纳米胞状Cu2O微观结构的影响。观察结果表明，随着腐蚀时间的延长，两种结构均变粗，纳米胞状Cu2O进一步氧化为纳米层状氧化铜（CuO）。
A hierarchical trimodal structure comprised of micro-porous Gasar Cu, nano-porous Cu and nano-cellular cuprous oxide (Cu2O) was fabricated by dealloying Cu–Zn alloy layer on the inner surface of Gasar pores along with a spontaneous oxidation process. The influence of corrosion time on the microstructure of the resulting nano-porous Cu and nano-cellular Cu2O was investigated. Observed results showed that with the corrosion time increase, both of the structures were coarsened, and the nano-cellular Cu2O was further oxidized into nano-lamellar copper oxide (CuO).
登录
查看更多内容
影响因子：
64.8
作者：
M. Stratmann;M. Rohwerder
通讯作者：
M. Stratmann;M. Rohwerder
影响因子：
3
作者：
Xiaojun Zhang;Guangfeng Wang;Hai-Bo Wu;Di Zhang;Xiaoqing Zhang;Po Li;Hua-qiang Wu
通讯作者：
Xiaojun Zhang;Guangfeng Wang;Hai-Bo Wu;Di Zhang;Xiaoqing Zhang;Po Li;Hua-qiang Wu
影响因子：
2.3
作者：
Zhang Huawei;Li Yanxiang;Liu Yuan
通讯作者：
Zhang Huawei;Li Yanxiang;Liu Yuan
影响因子：
2.3
作者：
Chen Liu-Shou;Zhang Huawei;Liu Yuan;Li Yanxiang
通讯作者：
Chen Liu-Shou;Zhang Huawei;Liu Yuan;Li Yanxiang
DOI：
10.1016/j.mseb.2004.09.010
发表时间：
2005-01
影响因子：
3.6
作者：
G. Lu;Chunxi Li;Wenchuan Wang;Zi-hao Wang;J. Guan;H. Xia
通讯作者：
G. Lu;Chunxi Li;Wenchuan Wang;Zi-hao Wang;J. Guan;H. Xia