以AlCr 2+和C为原料，采用一种新的反应路线制备Cr2 AlC。将AlCr 2+和C粉在1400°C、20 MPa、Ar气氛下热压1h，得到Cr2 AlC块体陶瓷。研究了在1050-1400°C温度范围内形成Cr2 AlC的机理。结果表明，Cr2 AlC是由C和AlCr 2反应直接生成的。采用差热分析、X射线衍射、扫描电镜等手段对反应过程、物相组成和显微结构进行了表征。所制备的Cr2 AlC陶瓷在Ar气氛中高达1500°C是稳定的，但在1500°C以上分解成Al 8 Cr 5和Cr23 C6。
A new reaction route with AlCr2and C as starting materials has been developed to produce Cr2AlC. A Cr2AlC bulk ceramic was achieved by hot pressing the AlCr2and C powders at 1400°C with 20MPa for 1h in Ar. The mechanism to form Cr2AlC in a temperature range of 1050–1400°C was studied. It was confirmed that Cr2AlC is formed directly by a reaction between C and AlCr2. The reaction process, phase composition and microstructure were characterized with differential thermal analysis, X-ray diffractometry and scanning electron microscopy. The produced Cr2AlC ceramic is stable up to 1500°C in an Ar atmosphere, but decomposes into Al8Cr5and Cr23C6above 1500°C.
登录
查看更多内容
DOI：
10.1016/j.msea.2010.05.093
发表时间：
2010-08
影响因子：
6.4
作者：
Wenbo Yu;Shibo Li;W. Sloof
通讯作者：
Wenbo Yu;Shibo Li;W. Sloof
单质粉末机械活化烧结Ti3AlC2的合成及微观结构
影响因子：
5.2
作者：
Zhang, Zhi-Li;Zhou, Yang;Li, Shi-Bo;Bei, Guo-Ping;Zhai, Hong-Xiang
通讯作者：
Zhai, Hong-Xiang
影响因子：
5.7
作者：
S. Li;Wenbo Yu;Hongxiang Zhai;G. Song;W. Sloof;S. Zwaag
通讯作者：
S. Li;Wenbo Yu;Hongxiang Zhai;G. Song;W. Sloof;S. Zwaag
影响因子：
6.2
作者：
I. Salama;T. El-Raghy;M. Barsoum
通讯作者：
I. Salama;T. El-Raghy;M. Barsoum
影响因子：
3.9
作者：
W. Tian;Pei-ling Wang;Guo‐Jun Zhang;Y. Kan;Yongxiang Li
通讯作者：
W. Tian;Pei-ling Wang;Guo‐Jun Zhang;Y. Kan;Yongxiang Li