Giant magnetoresistance in fine particle of La0.67Ca0.33MnO3 synthesized at low temperatures
Giant magnetoresistance in fine particle of La0.67Ca0.33MnO3 synthesized at low temperatures
复制标题
DOI：
10.1063/1.116780
复制
发表时间：
1996
影响因子：
4
通讯作者：
R. Sánchez;J. Rivas;C. Vázquez-Vázquez-C.-Vázquez-Vázquez-1397107083;†. A. M. A. López-Quintela-†.-A.-M.-A.-López-Quintela-2093757934;M. Causa;M. Tovar;S. Oseroff
中科院分区：
文献类型：
--
作者：
R. Sánchez;J. Rivas;C. Vázquez-Vázquez-C.-Vázquez-Vázquez-1397107083;†. A. M. A. López-Quintela-†.-A.-M.-A.-López-Quintela-2093757934;M. Causa;M. Tovar;S. Oseroff
使用溶胶-凝胶法，我们在540至1000 ° C的温度下制备了20至110 nm范围内的La0.67Ca0.33MnO3单分散颗粒。在1 kOe的磁场中，所有颗粒尺寸的磁阻均大于10%。这些结果可能与未来的应用有关。
Using a sol‐gel method we have prepared monodispersive particles of La0.67Ca0.33MnO3 in the range from 20 to 110 nm at temperatures from 540 to 1000 °C. A magnetoresistance above 10% was obtained in a field of 1 kOe for all the particles sizes. These results may be relevant for future applications.