First-principles study of defect energetics in titanium-doped alumina
First-principles study of defect energetics in titanium-doped alumina
复制标题
DOI：
10.1103/physrevb.68.214102
复制
发表时间：
2003-12
影响因子：
3.7
通讯作者：
K. Matsunaga;A. Nakamura;Takahisa Yamamoto;Y. Ikuhara
中科院分区：
文献类型：
--
作者：
K. Matsunaga;A. Nakamura;Takahisa Yamamoto;Y. Ikuhara
First-principles plane-wave pseudopotential calculations were performed to study electronic structures, structural relaxation, and energetics of point defects in Ti-doped ${\mathrm{Al}}_{2}{\mathrm{O}}_{3}.$ Substitutional and interstitial Ti ions with charge compensating intrinsic defects were considered, and their formation energies were evaluated under various atomic chemical potentials. It was found that substitutional ${\mathrm{Ti}}^{4+}$ ions with charge compensating Al vacancies were most stable in the oxidized condition. In contrast, as oxygen chemical potentials decreased, the formation energy of substitutional ${\mathrm{Ti}}^{3+}$ decreased to have the smallest value in the relatively reduced conditions. However, in the intermediate range of oxygen potentials, substitutional ${\mathrm{Ti}}^{3+}$ and ${\mathrm{Ti}}^{4+}$ exhibited similar formation energies, indicating that these Ti defects can coexist in a particular reduction environment.
First-principles plane-wave pseudopotential calculations were performed to study electronic structures, structural relaxation, and energetics of point defects in Ti-doped ${\mathrm{Al}}_{2}{\mathrm{O}}_{3}.$ Substitutional and interstitial Ti ions with charge compensating intrinsic defects were considered, and their formation energies were evaluated under various atomic chemical potentials. It was found that substitutional ${\mathrm{Ti}}^{4+}$ ions with charge compensating Al vacancies were most stable in the oxidized condition. In contrast, as oxygen chemical potentials decreased, the formation energy of substitutional ${\mathrm{Ti}}^{3+}$ decreased to have the smallest value in the relatively reduced conditions. However, in the intermediate range of oxygen potentials, substitutional ${\mathrm{Ti}}^{3+}$ and ${\mathrm{Ti}}^{4+}$ exhibited similar formation energies, indicating that these Ti defects can coexist in a particular reduction environment.