Effect of absorbers' composition on the microwave absorbing performance of hollow Fe3O4 nanoparticles decorated CNTs/graphene/C composites
Effect of absorbers' composition on the microwave absorbing performance of hollow Fe3O4 nanoparticles decorated CNTs/graphene/C composites
复制标题
DOI：
10.1016/j.jallcom.2018.03.202
复制
发表时间：
2018-06
影响因子：
6.2
通讯作者：
Kaichuang Zhang;Qian Zhang;Xinbao Gao;Xuefang Chen;Yi Wang;Wangchao Li;Jingyi Wu
中科院分区：
文献类型：
--
作者：
Kaichuang Zhang;Qian Zhang;Xinbao Gao;Xuefang Chen;Yi Wang;Wangchao Li;Jingyi Wu
Hollow Fe3O4nanoparticles decorated CNTs/graphene/C composites were successfully synthesized using a facile solvent method and a process of high temperature calcination. In addition, in order to research the effect of absorbers' composition on the microwave absorbing performance, hollow Fe3O4nanoparticles decorated CNTs/C composites and the hollow Fe3O4nanoparticles decorated graphene/C composites were also synthesized. As EM wave absorbers, we tested the electromagnetic absorption properties of the paraffin composites containing 20 wt% of the prepared composites. The maximum reflection loss of the three paraffin composites was −54.43 dB, −39.52 dB and −45.40 dB at 11.4 GHz, 9.7 GHz and 7.8 GHz with a thickness of 1.9 mm, 2.4 mm and 2.8 mm, respectively. The absorption bandwidth (<-10 dB) of the maximum reflection loss value was 3.2 GHz, 2.72 GHz and 2.8 GHz, respectively. The excellent electromagnetic absorption properties were attributed to the special structure and ingredients, impedance matching and microwave attenuation.