讨论在下文中，我们结合了不同实验方法的特征值，以获得这些合金的结晶行为的一致图像。 DSC 测量以 10 K/min 的加热速率进行，即这些实验在 T g 和 T x 附近的时间尺度约为一分钟。因此，我们将 DSC 玻璃化转变温度和结晶温度分别表示为 T g (1 分钟) 和 T x (1 分钟)。根据 XRD 测量，我们得出结论
DiscussionIn the following, we combine the characteristic values of the different experimental methods in order to obtain a consistent picture for the crystallization behavior of these alloys. The DSC measurements have been performed at a heating rate of 10 K/min, ie, the time scales of these experiments near T g and T x are of the order of one minute. Therefore, we denote the DSC glass transition and crystallization temperature as T g (1 min) and T x (1 min), respectively. From the XRD measurements, weConclusions