CuS@Cu freestanding electrode via electrochemical corrosion for high performance Li-ion batteries
CuS@Cu freestanding electrode via electrochemical corrosion for high performance Li-ion batteries
复制标题
通过电化学腐蚀的CuS@Cu独立电极用于高性能锂离子电池
DOI：
10.1016/j.matlet.2017.04.120
复制
发表时间：
2017-08
影响因子：
3
通讯作者：
Xuelin Yang
中科院分区：
文献类型：
--
作者：
Jun Tang;Shibing Ni;Qichang Chen;Jicheng Zhang;Xuelin Yang
采用h2o2辅助电化学腐蚀法制备了三维多孔CuS@Cu复合材料，该复合材料作为锂离子电池的独立电极具有优异的电化学性能。在0.5 a g−1的特定电流下，它不会产生容量衰减，在500次循环后显示放电/充电为845/834 mAh g−1。在0.1到1.5 A g−1的不同比电流下循环50次后，CuS@Cu电极在2 A g−1下循环300次后仍然没有出现容量衰减，放电容量为414 mAh g−1。
3D porous CuS@Cu composite is prepared via a facile H2O2aided electrochemical corrosion method, which shows prominent electrochemical performance as freestanding electrode for Li-ion batteries. It delivers no capacity fading at a specific current of 0.5 A g−1, showing discharge/charge of 845/834 mAh g−1after 500 cycles. After 50 cycles at various specific current from 0.1 to 1.5 A g−1, the CuS@Cu electrode can still exhibit no capacity fading over 300 cycles at 2 A g−1, delivering discharge capacity of 414 mAh g−1.
登录
查看更多内容
影响因子：
2.1
作者：
Y. Zhang;X. Hu;Tao Qiao
通讯作者：
Y. Zhang;X. Hu;Tao Qiao
影响因子：
2.1
作者：
Zhanjun He;Yabo Zhu;Z. Xing;Zhengyuan Wang
通讯作者：
Zhanjun He;Yabo Zhu;Z. Xing;Zhengyuan Wang
影响因子：
9.2
作者：
Mingjiong Zhou;Na Peng;Z. Liu;Xiaobing Yun;Huiqiu He;Yonggao Xia;Zhaoping Liu;S. Okada
通讯作者：
Mingjiong Zhou;Na Peng;Z. Liu;Xiaobing Yun;Huiqiu He;Yonggao Xia;Zhaoping Liu;S. Okada
影响因子：
29.4
作者：
Cabana, Jordi;Monconduit, Laure;Rosa Palacin, M.
通讯作者：
Rosa Palacin, M.
影响因子：
6.2
作者：
Junxiang Wang;X. Lyu;Lingyun Wang;Shuang Yu;Weixue Zhu;Cui Han;Xiaoqiang Cao
通讯作者：
Junxiang Wang;X. Lyu;Lingyun Wang;Shuang Yu;Weixue Zhu;Cui Han;Xiaoqiang Cao