Compressional behaviour of carbon fibres
Compressional behaviour of carbon fibres
复制标题
DOI：
10.1007/bf00580133
复制
发表时间：
1990-12
影响因子：
4.5
通讯作者：
N. Melanitis;C. Galiotis
中科院分区：
文献类型：
--
作者：
N. Melanitis;C. Galiotis
The axial compressive strain to failure of various types of PAN-based carbon fibres was measured by applying small and defined compressive loads to single filaments which have been bonded to a rectangular polymer cantilever beam and parallel to its long edge. By monitoring the Raman frequencies along the fibre with the 2 μm laser probe of a Raman microscope, the critical compressive strain required for first fibre failure could be assessed and the residual load that each type of fibre supported after first failure, could be measured. Estimates of the compressive moduli for all fibres could, also, be obtained by considering the dependence of the Raman frequency upon compressive strain in the elastic region. The critical compressive strain to failure was found to decrease with fibre modulus and its value was, approximately, equal to 50% of the tensile fracture strain. However, for some low-modulus fibres the compressive strain to failure was found to approach the tensile fracture strain. The initial compressive moduli of high-modulus fibres were estimated to decrease up to a maximum of 10% with respect to their tensile moduli, whereas more significant reductions were found in the case of intermediate and low-modulus fibres.