STRUCTURE AND MAGNETIC PROPERTIES OF MANGANESE OXIDE NANOPARTICLES PREPARED BY ARC SUBLIMATION
STRUCTURE AND MAGNETIC PROPERTIES OF MANGANESE OXIDE NANOPARTICLES PREPARED BY ARC SUBLIMATION
复制标题
电弧升华法制备氧化锰纳米粒子的结构和磁性能
DOI：
10.1142/s0217984910025358
复制
发表时间：
2010-12
影响因子：
1.9
通讯作者：
Choi, C. J.
中科院分区：
文献类型：
--
作者：
Sohnel, T.;Wang, H. X.;Jiang, W.;Si, P. Z.;Lee, J. G.;Choi, C. J.
采用电弧升华法制备了尺寸分布窄的纳米氧化锰颗粒。虽然MnO是反铁磁的，但所制备的氧化锰纳米颗粒表现出铁磁行为，在5 K下的矫顽力和交换偏置分别高达417，065 A/m和162，099 A/m。我们将这些异常的磁性归因于亚铁磁性Mn 3 O 4的存在，未补偿的表面自旋及其与反铁磁性MnO的耦合。
Manganese oxide nanoparticles with narrow size distribution were prepared in large scale by arc sublimation of bulk MnO. Although MnO is antiferromagnetic, the as-prepared manganese oxide nanoparticles exhibit ferromagnetic behaviors with coercivity and exchange bias up to 417,065 A/m and 162,099 A/m at 5 K, respectively. We attribute these anomalous magnetic properties to the presence of ferrimagnetic Mn3O4, uncompensated surface spins and their coupling to the antiferromagnetic MnO.
登录
查看更多内容
影响因子：
8.6
作者：
A. Goodwin;M. Tucker;M. Dove;D. Keen
通讯作者：
A. Goodwin;M. Tucker;M. Dove;D. Keen
影响因子：
3.7
作者：
M. Jagadeesh;M. Seehra
通讯作者：
M. Jagadeesh;M. Seehra
影响因子：
3.2
作者：
T. Mcguire;W. A. Crapo
通讯作者：
T. Mcguire;W. A. Crapo
δ-MnO2 纳米盘及其磁性能
影响因子：
3.5
作者：
Guo, Lin;Wang, Ning;Yang, Shihe;Cao, Xia
通讯作者：
Cao, Xia
影响因子：
1.8
作者：
Yongqin Chang;D. Yu;Zhe Wang;Y. Long;Hongzhou Zhang;R. Ye
通讯作者：
Yongqin Chang;D. Yu;Zhe Wang;Y. Long;Hongzhou Zhang;R. Ye