Strong magnetocaloric effects in La1−zCez(Fex−yMnySi1−x)13 at low temperatures
Strong magnetocaloric effects in La1−zCez(Fex−yMnySi1−x)13 at low temperatures
复制标题
低温下 La1−zCez(Fex−yMnySi1−x)13 中的强磁热效应
DOI：
10.1063/1.2227631
复制
发表时间：
2006
影响因子：
4
通讯作者：
K. Fukamichi
中科院分区：
文献类型：
--
作者：
S. Fujieda;A. Fujita;N. Kawamoto;K. Fukamichi
通过调整组成，降低了La1−zCez(Fex−yMnySi1−x)13的居里温度TC，因此在La0.75Ce0.25(Fe0.850Mn0.035Si0.110)13中，零场冷却后在5K时观察到流动电子的变磁跃迁。结果表明，La1−zCez(FexMnySi1−x)13化合物在19 ~ 180K的较低磁场范围内表现出较强的磁热效应。因此，La1−zCez(Fex−yMnySi1−x)13化合物可用于低温工作的磁性制冷剂。
The Curie temperature TC of La1−zCez(Fex−yMnySi1−x)13 is decreased by adjusting the composition, and hence the itinerant-electron metamagnetic transition is observed at 5K in La0.75Ce0.25(Fe0.850Mn0.035Si0.110)13 after zero-field cooling. As a result, the La1−zCez(FexMnySi1−x)13 compounds exhibit strong magnetocaloric effects in relatively low magnetic fields in a wide range of temperatures between about 19 and 180K. Consequently, the La1−zCez(Fex−yMnySi1−x)13 compounds are useful for the magnetic refrigerants working at low temperatures.
影响因子：
2.1
作者：
S. Fujieda;A. Fujita;K. Fukamichi
通讯作者：
S. Fujieda;A. Fujita;K. Fukamichi
Ce部分取代La增强La(Fe_<0.90>Si_<0.10>)_<13>及其氢化物磁热效应
DOI：
--
发表时间：
2004
期刊：
Mater.Trans. 45
影响因子：
--
作者：
藤田麻哉 他;藤田麻哉 他;藤田麻哉 他;藤田麻哉 他;藤枝 俊 他
通讯作者：
藤枝 俊 他