Influence of heat-treatment on magnetic, magnetostrictive and piezomagnetic properties and structure of Fe64Ni10Nb3Cu1Si13B9 metallic glass
Influence of heat-treatment on magnetic, magnetostrictive and piezomagnetic properties and structure of Fe64Ni10Nb3Cu1Si13B9 metallic glass
复制标题
DOI：
10.1016/j.msea.2003.10.082
复制
发表时间：
2004-07-15
期刊：
影响因子：
6.4
通讯作者：
Minguez, P
中科院分区：
文献类型：
--
作者：
Kaczkowski, Z;Vlasák, G;Minguez, P
研究了Fe64Ni10Nb3Cu1Si13B9合金条状样品在100-600℃真空退火后的磁性能和压磁性能。矫顽力为5～50A/m，饱和磁感应强度为1.25T左右，磁致伸缩为(22-26)×10(-6)(退火至480℃后)。磁力耦合系数达到0.62，弹性模量从70 GPa变化到205 GPa。 (C) 2003 Elsevier B.V. 保留所有权利。
The magnetic and piezomagnetic properties of the strip-shaped samples of the Fe64Ni10Nb3Cu1Si13B9 alloy were investigated after annealing in vacuum in the temperature range 100-600degreesC. The coercivity was in the range from 5 to 50 A/m, the saturation induction about 1.25 T and magnetostriction (22-26) X 10(-6) (after annealing up to 480degreesC). The magnetomechanical coupling coefficient reached the value of 0.62, and the elasticity moduli were changing from 70 to 205 GPa. (C) 2003 Elsevier B.V. All rights reserved.