Short fatigue cracks in intermetallic γ-TiAl-alloys
Short fatigue cracks in intermetallic γ-TiAl-alloys
复制标题
金属间化合物γ-TiAl合金中的短疲劳裂纹
DOI：
10.1111/ffe.12323
复制
发表时间：
--
影响因子：
3.7
通讯作者：
Brueckner-Foit
中科院分区：
文献类型：
--
作者：
Wessel;Zeismann;Brueckner-Foit
研究了四种不同的γ-TiAl-合金的室温疲劳裂纹扩展及其与局部显微组织的关系，这些合金的显微组织从粗的和全层片到细的和部分层片。它示出，失效的周期数强烈地依赖于裂纹扩展的第一屏障的效率，因为裂纹生长速率可能会迅速增加，一旦这个屏障已被突破了一个特定的裂纹。利用高分辨率光学显微镜和扫描电子显微镜研究了两种典型势垒（群体边界和孪晶边界）的裂纹扩展行为。
Fatigue crack growth at room temperature and its relation to the local microstructure is studied for four different γ‐TiAl‐alloys with microstructures ranging from coarse and fully lamellar to fine and partly lamellar. It is shown that the number of cycles to failure depends strongly on the efficiency of the first barrier to crack extension, as crack growth rates may increase rapidly once this barrier has been breached by a specific crack. The crack extension behaviour for two typical barriers (colony boundary and twin boundary) is studied using high‐resolution optical and scanning electron microscopy.
登录
查看更多内容
泰坦与泰坦法律
影响因子：
4.5
作者：
M. Peters;C. Leyens
通讯作者：
C. Leyens
影响因子：
5.4
作者：
NEWMAN, JC;RAJU, IS
通讯作者：
RAJU, IS
金属间化合物 γ-TiAl 合金中微缺口的局部变形和裂纹萌生
DOI：
--
发表时间：
2016
期刊：
影响因子：
--
作者：
B. Bode;W. Wessel;A. Brueckner;J. Mildner;M. Wollenhaupt;T. Baumert
通讯作者：
T. Baumert
用于研究小裂纹生长的微凹口
影响因子：
3.7
作者：
Wessel;Mildner;Brueckner-Foit
通讯作者：
Brueckner-Foit
裂纹%20路径%20of%20PST%20晶体%20of%20二元%20Ti-49at.%Al%20合金
DOI：
--
发表时间：
1998
期刊：
影响因子：
--
作者：
Y. Lu;Yonggang Zhang;Cheng Chen
通讯作者：
Cheng Chen