Synthesis and characterization of arsenate/phosphate hydroxyapatite solid solution
Synthesis and characterization of arsenate/phosphate hydroxyapatite solid solution
复制标题
砷酸盐/磷酸盐羟基磷灰石固溶体的合成与表征
DOI：
10.1016/j.matlet.2009.02.036
复制
发表时间：
2009-05
影响因子：
3
通讯作者：
Liu, Huili
中科院分区：
文献类型：
--
作者：
Long, Fei;Zhang, Xuehong;Qian, Meifang;He, Na;Zhu, Yinian;Liu, Huili
采用水沉淀法直接制备了一系列砷酸盐取代羟基磷灰石。元素分析、XRD、FT-IR、SEM等表征研究证实了砷酸盐/磷酸羟基磷灰石固溶体的形成。XRD分析表明，单胞a和c参数并不像维加德定律所期望的那样随着取代度的变化而平滑变化。As/(P+As)=0.46 ~ 1.0的固体为典型针状结晶；As/(P+As)= 0-0.46的大表格。在FT-IR光谱中，随着砷酸盐比例的增加，磷酸盐峰的面积逐渐被抑制，而砷酸盐峰的面积逐渐增大。
A series of arsenate substituted hydroxyapatite was directly prepared through aqueous precipitation method. Characterization studies from elemental analysis, XRD, FT-IR spectra and SEM have confirmed the forming of the arsenate/phosphate hydroxyapatite solid solutions. The XRD analysis indicated that the unit cell a and c parameters did not vary smoothly with the degree of substitution as expected by the Vegard's Law. The solids with As/(P+As)=0.46–1.0 were typically needle-like crystals; those with As/(P+As)=0–0.46 large tabular. In FT-IR spectra, the area of the phosphate peak was gradually suppressed and that of the arsenate peak increased as the proportion of the arsenate increased.
登录
查看更多内容
影响因子：
11.4
作者：
Bothe, JV;Brown, PW
通讯作者：
Brown, PW
影响因子：
1.1
作者：
T. Narasaraju;U. S. Rai
通讯作者：
T. Narasaraju;U. S. Rai
影响因子：
1.8
作者：
M. Masaoka;A. Kyono;T. Hatta;M. Kimata
通讯作者：
M. Masaoka;A. Kyono;T. Hatta;M. Kimata
影响因子：
3.9
作者：
U. Becker;M. Prieto
通讯作者：
U. Becker;M. Prieto
影响因子：
3
作者：
A. Onda;Shuhei Ogo;K. Kajiyoshi;K. Yanagisawa
通讯作者：
A. Onda;Shuhei Ogo;K. Kajiyoshi;K. Yanagisawa