Nanoflake-modified MgO microspheres prepared by flame spraying
Nanoflake-modified MgO microspheres prepared by flame spraying
复制标题
火焰喷涂制备纳米片改性MgO微球
DOI：
10.1016/j.matlet.2013.10.068
复制
发表时间：
2014-01
影响因子：
3
通讯作者：
Yixiang Chen
中科院分区：
文献类型：
--
作者：
Guanghua Liu;Jiangtao Li;Feng Wang;Yixiang Chen
采用火焰喷涂法制备了Mg（OH）2纳米片修饰的MgO微球，微球粒径为15-70 μm，纳米片厚度约为10 nm。Mg（OH）2纳米片可以通过在350 °C下煅烧2 h转化为MgO，并且在该相转变期间，纳米片形态得到很好的保留。MgO微球具有微/纳米复合结构，比表面积为21.6 m2/g，流动性良好。MgO微球的带隙能量和折射率估计为Eg =5.5 eV和n =1.826。
Novel MgO microspheres modified with Mg(OH)2nanoflakes were prepared by flame spraying, where the microspheres were 15–70 μm, and the nanoflakes had a thickness of about 10 nm. The Mg(OH)2nanoflakes could be converted into MgO by calcination at 350 °C for 2 h, and during this phase transformation the nanoflake morphology was well preserved. With a micro/nano-complex structure, the MgO microspheres showed acceptable flowability and specific surface area of 21.6 m2/g. The bandgap energy and refractive index of the MgO microspheres were estimated to beEg=5.5 eV andn=1.826.
登录
查看更多内容
影响因子：
6.7
作者：
S. Ardizzone;C. Bianchi;B. Vercelli
通讯作者：
S. Ardizzone;C. Bianchi;B. Vercelli
影响因子：
3.3
作者：
J. A. Wang;O. Novaro;X. Bokhimi;T. López;R. Gómez;J. Navarrete;M. E. Llanos;E. López-Salinas
通讯作者：
J. A. Wang;O. Novaro;X. Bokhimi;T. López;R. Gómez;J. Navarrete;M. E. Llanos;E. López-Salinas
DOI：
10.1149/1.2404256
发表时间：
1971
期刊：
--
影响因子：
--
作者：
J. Pankove
通讯作者：
J. Pankove
影响因子：
2.8
作者：
Hannaneh Heidari;M. Abedini;A. Nemati;M. Amini
通讯作者：
Hannaneh Heidari;M. Abedini;A. Nemati;M. Amini
影响因子：
1.8
作者：
Lv, JP;Qiu, LZ;Qu, BJ
通讯作者：
Qu, BJ