Characteristics of crack patterns controlling the retained strength of ceramics after thermal shock
Characteristics of crack patterns controlling the retained strength of ceramics after thermal shock
复制标题
DOI：
10.1007/s11706-010-0089-x
复制
发表时间：
2010-07
期刊：
影响因子：
--
通讯作者：
Ze Zhang;Y. Shao;F. Song
中科院分区：
文献类型：
--
作者：
Ze Zhang;Y. Shao;F. Song
The physical mechanisms that determine the retained strength of ceramics after thermal shock are studied by measuring experimentally and statistically the density and depth of cracks produced in the interior of the ceramics. The analysis indicates that the key factor controlling the retained strength is the maximum depth of cracks rather than the density of cracks in the ceramics. The result presented here forms a basis to further understand the thermal shock behavior of ceramics.