Microstructures developed by super-rapid induction heating-and-quenching (SRIHQ) of Fe-1.4%Cr-1%C pearlitic steel
Microstructures developed by super-rapid induction heating-and-quenching (SRIHQ) of Fe-1.4%Cr-1%C pearlitic steel
复制标题
显微组织%20发达%20by%20超快速%20感应%20加热淬火%20(SRIHQ)%20of%20Fe-1.4%Cr-1%C%20珠光体%20钢
DOI：
10.1016/j.msea.2013.04.024
复制
发表时间：
2013
期刊：
影响因子：
--
通讯作者：
S. Hata
中科院分区：
文献类型：
--
作者：
Y. Koizumi;T. Otsuka;Y. Minamino;T. Takayama;M. Ueyama;T. Daio;S. Hata
研究了一种Fe-1.4%Cr-1%C珠光体钢在不同条件下的超快速感应加热淬火组织和硬度。形成了由两种不同类型的马氏体（高孪晶或含有高位错密度）组成的纳米级层状组织，在0.5s加热至1223K后淬火，获得了最大硬度。电子能量损失谱分析表明，在srihq工艺实现的非均匀溶质分布中，两种不同类型的马氏体的形成取决于局部溶质浓度。
Microstructures and hardness of a Fe–1.4%Cr–1%C pearlitic steel processed by super-rapid induction heating-and-quenching (SRIHQ) under various conditions have been investigated. A nano-scaled laminated microstructure composed of two different types of martensite (highly-twinned or containing a high dislocation density) was formed and the maximum hardness was obtained by heating to 1223K in 0.5s and quenched. Electron energy loss spectroscopy indicated that the two different types of martensite were formed depending on the local solute-concentration in the non-uniform solute-distribution realized by the SRIHQ-process.
Fe-8.2Cr-C合金中奥氏体的形成和碳化物的溶解
DOI：
10.1515/ijmr-1999-900106
发表时间：
1999
期刊：
International Journal of Materials Research - Zeitschrift für Metallkunde
影响因子：
--
作者：
D. Shtansky;K. Nakai;Y. Ohmori
通讯作者：
Y. Ohmori
超快速感应加热淬火铁素体球墨铸铁的疲劳强度
DOI：
10.2320/matertrans.45.2930
发表时间：
2004
期刊：
影响因子：
--
作者：
Y. Misaka;Kazuhiro Kawasaki;J. Komotori;M. Shimizu
通讯作者：
M. Shimizu
透射电子显微镜
DOI：
10.1007/978-3-319-26651-0_3
发表时间：
2016
期刊：
--
影响因子：
--
作者：
Burke M
通讯作者：
Burke M