Microwave dielectric properties and compatibility with silver of low-fired Li2Cu0.1Zn0.9Ti3O8 ceramic
Microwave dielectric properties and compatibility with silver of low-fired Li2Cu0.1Zn0.9Ti3O8 ceramic
复制标题
低温烧制Li2Cu0.1Zn0.9Ti3O8陶瓷的微波介电性能及与银的相容性
DOI：
10.1016/j.matlet.2012.04.120
复制
发表时间：
2012-08
影响因子：
3
通讯作者：
Zhang, Hui
中科院分区：
文献类型：
--
作者：
Fang, Liang;Liu, Qinwen;Su, Congxue;Liao, Wei;Zhang, Hui
首次研究了一种新型低损耗、低温烧结微波介质陶瓷Li_2Cu_（0.1）Zn_（0.9）Ti_3 O_8。采用常规固相法制备了单相尖晶石结构的纯Li 2Cu 0. 1 Zn 0. 9 Ti 3 O 8陶瓷，并在900°C ~ 975°C烧结2 h。在950°C/2 h烧结的陶瓷具有中等的介电常数（εr）为25.2，高品质因数（Q×f）为32 100 GHz，谐振频率温度系数（τf）为1.6ppm/ °C，接近于零。Li2Cu0.1Zn0.9Ti3O8陶瓷可与Ag电极相容，是一种很有前途的LTCC陶瓷材料。
A new low-loss, low-temperature sinterable microwave dielectric ceramic Li2Cu0.1Zn0.9Ti3O8was investigated for the first time. Single phase pure Li2Cu0.1Zn0.9Ti3O8ceramic with cubic spinel structure was obtained by the conventional solid-state route and sintered at 900°C–975°C for 2h. The ceramic sintered at 950°C/2h exhibits a moderate dielectric constant (εr) of 25.2, a high quality factor value (Q×f) of 32 100GHz, and a near-zero temperature coefficient of the resonant frequency (τf) of 1.6ppm/ °C. The Li2Cu0.1Zn0.9Ti3O8ceramic can be compatible with Ag electrode, which makes it a promising ceramic for LTCC technology application.
登录
查看更多内容
影响因子：
6.2
作者：
Fang, Liang;Chu, Dongjin;Huang, Xi
通讯作者：
Huang, Xi
影响因子：
1.5
作者：
A. Kan;H. Ogawa;H. Ohsato;Junji Sugishita
通讯作者：
A. Kan;H. Ogawa;H. Ohsato;Junji Sugishita
影响因子：
3.9
作者：
Di Zhou;C. Randall;L. Pang;Hong Wang;Xinguang Wu;Jing Guo;Gao-qun Zhang;L. Shui;X. Yao
通讯作者：
Di Zhou;C. Randall;L. Pang;Hong Wang;Xinguang Wu;Jing Guo;Gao-qun Zhang;L. Shui;X. Yao
影响因子：
3.9
作者：
L. Fang;Chunchun Li;X. Peng;Changzheng Hu;Bo-lin Wu;Huangfu Zhou
通讯作者：
L. Fang;Chunchun Li;X. Peng;Changzheng Hu;Bo-lin Wu;Huangfu Zhou
影响因子：
3
作者：
L. Pang;Di Zhou
通讯作者：
L. Pang;Di Zhou