Microleakage in restorations with glass ionomer liners after thermocycling.
Microleakage in restorations with glass ionomer liners after thermocycling.
复制标题
热循环后玻璃离聚物内衬修复体中的微渗漏。
DOI：
10.1016/0300-5712(90)90095-v
复制
发表时间：
1990
影响因子：
4.4
通讯作者：
M. J. Wagner
中科院分区：
文献类型：
--
作者：
C. Arcoria;B. Vitasek;J. Dewald;M. J. Wagner
本研究的目的是比较热循环后两种内衬聚烯烃酸盐（玻璃离子）粘固剂的修复体周围的微渗漏。在48颗磨牙的直径和深度为2.0 mm的准备。一半的准备内衬玻璃离子，其余的没有内衬。放置牙科汞合金或玻璃离子修复材料，汞合金保持未磨光和未抛光。在4°C和50°C之间热循环选择的纯化物625次。将牙齿浸入0.5%亚甲蓝溶液中，切片，并在100倍放大倍率下目视评分微渗漏。数据分析表明，微渗漏的显着差异，因为。热循环（χ2= 103.38，d.f. = 19，2 P < 0.0004）;玻璃离子衬垫的存在（χ2= 53.28，d.f. = 19，2 P < 0.0001）和修复材料类型（χ2= 103.44，d.f. = 19，2P< 0.0004）。玻璃离子衬垫的使用显着减少微渗漏，在汞合金和玻璃离子充填时，受到热循环。
The purpose of this study was to compare microleakage around two types of restorations lined with polyalkenoate (glass ionomer) cements after thermocycling. Preparations were made in 48 molars to a diameter and depth of 2.0 mm. Half of the preparations were lined with glass ionomer, and the remainder were not lined. Dental amalgam or glass ionomer restorative material was placed and the amalgams were left unburnished and unpolished. Selected restorations were thermocycled 625 times between 4°C and 50°C. Teeth were immersed in 0.5 per cent methylene blue solution, sectioned and visually scored for microleakage at × 100 magnification. Data analysis indicated significant differences in microleakage because of. thermocycling (χ2= 103.38, d.f. = 19, 2P< 0.0004); presence of glass ionomer liners (χ2= 53.28, d.f. = 19, 2P< 0.0001); and type of restorative material (χ2= 103.44, d.f. = 19, 2P< 0.0004). The use of a glass ionomer liner significantly reduced microleakage in both amalgam and glass ionomer restorations when subjected to thermocycling.
传统和高铜汞合金修复体的微渗漏。
DOI：
10.1016/0022-3913(85)90511-6
发表时间：
1985
期刊：
The Journal of prosthetic dentistry
影响因子：
--
作者：
Gottlieb,EW;Retief,DH;Bradley,EL
通讯作者：
Bradley,EL
牙本质粘合剂和牙齿结构之间的粘合耐久性。
DOI：
10.1016/0022-3913(89)90326-0
发表时间：
1989
期刊：
The Journal of prosthetic dentistry
影响因子：
--
作者：
Davis,EL;Joynt,RB;WieczkowskiJr,G;Laura,JC
通讯作者：
Laura,JC