Fully sealed, high-brightness carbon-nanotube field-emission display
Fully sealed, high-brightness carbon-nanotube field-emission display
复制标题
DOI：
10.1063/1.125253
复制
发表时间：
1999-11-15
影响因子：
4
通讯作者：
Kim, JM
中科院分区：
文献类型：
--
作者：
Choi, WB;Chung, DS;Kim, JM
一个完全密封的场发射显示器4.5英寸。在尺寸上已经使用单壁碳纳米管（CNT）-有机粘合剂制造。所制造的显示器在低于415摄氏度的低温下是完全可扩展的，并且使用膏挤压和表面摩擦技术垂直对准CNT。在3V/μ m（J = 90 μ A/cm（2））下，观察到1V/μ m的开启电场和1.5mA的场发射电流。在4.5英寸的整个面积上观察到在3.7 V/μ m下1800 cd/m（2）的亮度。面板从绿色磷铟锡氧化物玻璃。发现电流的波动在4.5英寸范围内约为7%。阴极面积(C)1999年美国物理学会。[S0003-6951（99）00746-9]。
A fully sealed field-emission display 4.5 in. in size has been fabricated using single-wall carbon nanotube (CNT)-organic binders. The fabricated displays were fully scalable at low temperature, below 415 degrees C, and CNTs were vertically aligned using paste squeeze and surface rubbing techniques. The turn-on fields of 1 V/mu m and field emission current of 1.5 mA at 3 V/mu m (J = 90 mu A/cm(2)) were observed. Brightness of 1800 cd/m(2) at 3.7 V/mu m was observed on the entire area of a 4.5 in. panel from the green phosphor-indium-tin-oxide glass. The fluctuation of the current was found to be about 7% over a 4.5 in. cathode area. (C) 1999 American Institute of Physics. [S0003-6951(99)00746-9].