Transformation behaviour of Ti–Ni and Ti–Ni–Cu alloy ribbons with nano Ti2Ni particles
Transformation behaviour of Ti–Ni and Ti–Ni–Cu alloy ribbons with nano Ti2Ni particles
复制标题
DOI：
10.1016/j.msea.2006.02.245
复制
发表时间：
2007-03
期刊：
影响因子：
6.4
通讯作者：
T. Nam;Jae-hwa Lee;D. Jung;Cheol-am Yu;Yinong Liu;Yeon-wook Kim
中科院分区：
文献类型：
--
作者：
T. Nam;Jae-hwa Lee;D. Jung;Cheol-am Yu;Yinong Liu;Yeon-wook Kim
Ti–Ni and Ti–Ni–Cu alloy ribbons have been prepared by single roll melt spinning, and then martensitic transformation behaviours were investigated by means of transmission electron microscopy, differential scanning calorimetry and X-ray diffraction. In 51Ti–49Ni(at.%) alloy ribbons, Ti2Ni particles of a size less than 50nm with the coherent interface with the matrix were found, while they were not found in 50Ti–50Ni alloy ribbons. In 49Ti–46Ni–5Cu and 50Ti–45Ni–5Cu alloy ribbons, Ti2Ni particles of size less than 30nm with coherent interface with the matrix were found. Coherent Ti2Ni particles induced the R phase transformation in Ti–Ni alloys, and consequently transformation occurred in two-stages, i.e., B2–R–B19. Coherent Ti2Ni particles induced the B19 martensite in a Ti–45Ni–5Cu alloy, and consequently transformation occurred in two-stages, i.e., B2–B19–B19′. The change in transformation behaviour was ascribed to strain fields developed around coherent Ti2Ni particles.