Influence of thermal aging on the SCC susceptibility of wrought 316LN stainless steel in a high temperature water environment
Influence of thermal aging on the SCC susceptibility of wrought 316LN stainless steel in a high temperature water environment
复制标题
DOI：
10.1016/j.corsci.2013.12.011
复制
发表时间：
2014-04
影响因子：
8.3
通讯作者：
M. Wang;Lei Chen;Xiao-Cui Liu;Xiaocong Ma
中科院分区：
文献类型：
--
作者：
M. Wang;Lei Chen;Xiao-Cui Liu;Xiaocong Ma
Influence of thermal aging at non-sensitized temperature on the SCC susceptibility of wrought 316LN at high temperature water was investigated. The SCC susceptibility increases with increasing of aging time, especially over 1000 h. The fracture surface for aged samples shows a mixed mode. In particular, the intergranular attack (IGA) has been found in brittle surface of the long-term aged material (5000 h). Kinks and dislocations at the grain boundary (GB) have been found as well as aging-induced hardening. Carbon enrichment on the GB is believed to be an important cause of IGA and higher SCC susceptibility in aged materials.