アルミナ粒子分散型Al-Cu-Mg系複合材料の時効析出
アルミナ粒子分散型Al-Cu-Mg系複合材料の時効析出
复制标题
氧化铝颗粒弥散Al-Cu-Mg复合材料的时效析出
DOI：
10.2464/jilm.41.752
复制
发表时间：
1991
期刊：
影响因子：
--
通讯作者：
静夫 多々
中科院分区：
文献类型：
--
作者：
進 池野;一浩 川島;健二 松田;博之 穴田;静夫 多々
Aging behaviour of Al2O3-particle-dispersed (20vol%) Al-3.96%Cu and Al-4.09%Cu-1.58%Mg alloy composite materials was investigated by means of microvickers hardness, electrical resistivity measurements and transmission electron microscopy. In a case of an Al2O3/Al-3.96%Cu composite materials θ' phase precipitates on subgrain boundaries at an early stage of aging at 423K. After a prolonged agings an increased number of θ' precipitates are seen inside grains. While GP zones form normally in an Al-3.96%Cu alloy at this aging condition, no GP zones precipitate in the Al2O3/Al-3.96%Cu composite material and age-hardening does not take place. On the contrary, age-hardening is clearly observed in an Al2O3/Al-4.09%Cu-1.58%Mg composite material aged at 423K. In this composite material, both GP zones and θ' precipitates are found inside grains, being different from GPB zones and S' intermediate phases normally formed in an Al-4.09%Cu-1.58%Mg alloy.