The role of δ phase for fatigue crack propagation behavior in a Ni base superalloy at room temperature
The role of δ phase for fatigue crack propagation behavior in a Ni base superalloy at room temperature
复制标题
δ 相对室温镍基高温合金疲劳裂纹扩展行为的作用
DOI：
10.1016/j.msea.2016.12.029
复制
发表时间：
2017-01
期刊：
影响因子：
--
通讯作者：
Xiu Song
中科院分区：
文献类型：
--
作者：
Jinlan An;Lei Wang;Yang Liu;Wenliang Cai;Xiu Song
研究了不同δ相体积分数的镍基高温合金的室温疲劳裂纹扩展行为。结果表明，随着δ相体积分数的增加，合金的疲劳裂纹扩展速率增大，而疲劳裂纹扩展阻力和强度均降低。δ相对裂纹扩展行为的影响主要取决于δ相颗粒的低长径比对位错滑移的阻挡作用。另一方面，长针状δ相周围易产生位错堆积，导致应力集中。这种应力集中导致δ相从基体中剥离，并使裂纹易于沿无析出相区（PFZ）周围的长针状δ相沿着扩展。
The fatigue crack propagation behavior of a Ni base superalloy at room temperature with various volume fractions of δ phase was investigated. The result shows that fatigue crack growth rate of the alloy increases as δ phase volume fraction increases, while both the fatigue crack propagation resistance and the strength of the alloy decrease. The characteristic of δ phase on crack propagation behavior is depended on the dislocations slipping blocked by granular δ phase with low length-diameter radio. On the other hand, dislocations easily piled up around long needle-like δ phase which leads to stress concentration. This stress concentration causes δ phase debonding from the matrix and helps the crack easy propagates along long needle-like δ phase surrounded by precipitates free zone (PFZ).
登录
查看更多内容
影响因子：
5.4
作者：
S. Henkel;D. Holländer;M. Wünsche;H. Theilig-;P. Hübner;H. Biermann;S. Mehringer
通讯作者：
S. Henkel;D. Holländer;M. Wünsche;H. Theilig-;P. Hübner;H. Biermann;S. Mehringer
影响因子：
2.4
作者：
W. Burton;S. Mahmoud;K. Lease
通讯作者：
W. Burton;S. Mahmoud;K. Lease
影响因子：
6
作者：
Hanlon, T;Kwon, YN;Suresh, S
通讯作者：
Suresh, S
DOI：
10.1111/j.1460-2695.1987.tb01153.x
发表时间：
1987-02
影响因子：
3.7
作者：
K. Miller
通讯作者：
K. Miller
DOI：
10.1007/bf02646402
发表时间：
1978-04
期刊：
Metallurgical Transactions A
影响因子：
--
作者：
M. Clavel;André Pineau
通讯作者：
M. Clavel;André Pineau