Effect of temperature on in-use stiction of cantilever beams coated with perfluorinated alkysiloxane monolayers
Effect of temperature on in-use stiction of cantilever beams coated with perfluorinated alkysiloxane monolayers
复制标题
DOI：
10.1109/jmems.2006.878893
复制
发表时间：
2006-08-01
影响因子：
2.7
通讯作者：
Carraro, Carlo
中科院分区：
文献类型：
--
作者：
Frechette, Joelle;Maboudian, Roya;Carraro, Carlo
The effect of annealing (for temperatures up to 300 degrees C) on the antistiction performance of perfluorinated self-assembled monolayers (SAMs) is characterized using polycrystalline Si cantilever beam arrays. The monolayers 1H,1H,2H,2H, perfluorodecyltrichlorosilane (FDTS) and 1H,1H,2H,2H, perfluorodecyldimethylchlorosilane (FDDMCS) deposited from both liquid and vapor phase are investigated. It is observed that stiction decreases upon annealing for both monolayers and for both types of deposition. FDTS, however, displays greater temperature stability than FDDMCS regardless of the mode of deposition. The higher thermal resistance of the FDTS underscores the importance of monolayer crosslinking since unlike FDDMCS, FDTS forms a siloxane network on the surface. Further vacuum annealing and X-ray photoelectron spectroscopy experiments are performed to identify chemical changes in the monolayer during annealing. Incipient monolayer degradation is observed, with loss of the whole fluorinated monolayer chain. This process appears drastically different from the decomposition mechanism of hydrogenated alkylsiloxane monolayers such as octadecyltrichlorosilane (OTS).