Shear stress induced reduction of glass transition temperature in a bulk metallic glass
Shear stress induced reduction of glass transition temperature in a bulk metallic glass
复制标题
剪切应力导致块体金属玻璃的玻璃化转变温度降低
DOI：
10.1016/j.actamat.2005.03.015
复制
发表时间：
2005-06
期刊：
影响因子：
9.4
通讯作者：
中科院分区：
文献类型：
--
作者：
与先前观察到的玻璃化转变温度（Tg）在静水压力下略有增加相反，我们首次报告了Tg的急剧降低（40 K/500 MPa）剪切应力作用下的Zr46.75Ti8.25Cu7.5Ni10.0Be27.5大块非晶合金，这引起了在施加压缩应力时流动温度急剧下降的实验观察。T的显著降低归因于在剪切应力（126 Ω 3）下有较大的弛豫激活体积ΔVτ，并可用自由体积模型进行定量解释。
In contrast to previous observations of a slight increase in glass transition temperature (Tg) under hydrostatic pressure, we report, for the first time, a drastic reduction of Tg(40K/500MPa) induced by shear stress in a Zr46.75Ti8.25Cu7.5Ni10.0Be27.5bulk metallic glass, which gives rise to the experimental observation of the drastic decrease in flow temperature while a compressive stress was applied. The significant Tgreduction is attributed to a large activation volume of relaxation ΔVτunder shear stress (126Å3), and can be quantitatively interpreted in terms of the free volume model.
登录
查看更多内容
DOI：
10.1016/0921-5093(94)90211-9
发表时间：
1994-05
影响因子：
6.4
作者：
B. Zappel;F. Sommer
通讯作者：
B. Zappel;F. Sommer
影响因子：
2.7
作者：
K. Flores;D. Suh;R. Dauskardt;P. Asoka-kumar;P. Sterne;R. Howell
通讯作者：
K. Flores;D. Suh;R. Dauskardt;P. Asoka-kumar;P. Sterne;R. Howell
DOI：
10.1016/0001-6160(79)90055-5
发表时间：
1979-01-01
期刊：
ACTA METALLURGICA
影响因子：
--
作者：
ARGON, AS
通讯作者：
ARGON, AS
影响因子：
3.7
作者：
P. Wen;M. Tang;M. Pan;D. Zhao;Z. Zhang;Weihua Wang
通讯作者：
P. Wen;M. Tang;M. Pan;D. Zhao;Z. Zhang;Weihua Wang
DOI：
10.1016/0025-5416(79)90033-8
发表时间：
1979-04
期刊：
Materials Science and Engineering
影响因子：
--
作者：
J. Megusar;A. Argon;N. Grant
通讯作者：
J. Megusar;A. Argon;N. Grant