Coercivity enhancement in Dy-free Nd–Fe–B sintered magnets by using Pr-Cu alloy
Coercivity enhancement in Dy-free Nd–Fe–B sintered magnets by using Pr-Cu alloy
复制标题
Pr-Cu合金增强无镝Nd-Fe-B烧结磁体的矫顽力
DOI：
10.1063/1.4879898
复制
发表时间：
2014-05
期刊：
影响因子：
--
通讯作者：
Zhiwei Deng
中科院分区：
文献类型：
--
作者：
Jinbo Yang;Yingchang Yang;Jie Chen;Zhiwei Deng
The grain boundary phase of Dy-free sintered Nd-Fe-B magnets is modified by using Pr68Cu32 eutectic alloy. The coercivity of the modified magnets reaches 21 kOe, which is the highest value in Dy-free Nd-Fe-B sintered magnets. Microstructural investigations show that a smooth and thick grain boundary layer is formed, and the content of the ferromagnetic elements in the grain boundary layer decreases from 65 at. % to 9 at. %. In addition, the mean grain size (4.5 μm) in the doped sintered magnets is smaller than that (6.5 μm) in the original sintered magnets. The modification in grain boundary and grain size reduces the magnetic interactions among grains and hinders nucleation of reversed magnetic domains, resulting in a coercivity enhancement.
登录
查看更多内容
DOI：
10.1063/1.342309
发表时间：
1988-11
期刊：
--
影响因子：
--
作者：
J. Strzeszewski;G. Hadjipanayis;A. Kim
通讯作者：
J. Strzeszewski;G. Hadjipanayis;A. Kim
HDDR 近化学计量三元 Nd-Fe-B 粉末矫顽力增强
影响因子：
2.7
作者：
Yingchang Yang;Aizhi Sun;Fuqiang Yang;Renbo Song
通讯作者：
Renbo Song
影响因子：
3.2
作者：
B. Grieb;C. Pithan;E. Henig;G. Petzow
通讯作者：
B. Grieb;C. Pithan;E. Henig;G. Petzow
影响因子：
2.7
作者：
F. Vial;F. Joly;E. Nevalainen;M. Sagawa;K. Hiraga;K. T. Park
通讯作者：
F. Vial;F. Joly;E. Nevalainen;M. Sagawa;K. Hiraga;K. T. Park
影响因子：
2.1
作者：
R. Pollard;P. Grundy;S. Parker;D. G. Lord
通讯作者：
R. Pollard;P. Grundy;S. Parker;D. G. Lord