Corrosion protection mechanism of 2-mercaptobenzothiazole and its potential synergistic effect with cerium ions for treatment of AA 2024-T3
Corrosion protection mechanism of 2-mercaptobenzothiazole and its potential synergistic effect with cerium ions for treatment of AA 2024-T3
复制标题
DOI：
10.1016/j.jelechem.2020.114081
复制
发表时间：
2020-04-15
影响因子：
4.5
通讯作者：
Thompson, G. E.
中科院分区：
文献类型：
--
作者：
Balaskas, A. C.;Curioni, M.;Thompson, G. E.
研究了 2-巯基苯并噻唑 (2-MBT) 的腐蚀防护机制及其与氯化铈 (CeCl3) 对航空航天合金 AA 2024-T3 可持续性的潜在协同效应。通过图像辅助电化学噪声、分体电池技术、动电位极化、电化学阻抗谱 (EIS) 和扫描电子显微镜 (SEM) 观察来评估缓蚀剂 2-MBT 和 CeCl3 及其潜在的协同性能。这表明2-MBT抑制S相颗粒的脱合金并防止AA 2024-T3表面富铜颗粒的形成。 2-MBT 可保护第二相颗粒免受腐蚀，并通过在 AA 2024-T3 表面形成保护层，在 3.5% NaCl 溶液中提供可持续性。此外，在铝的阳极溶解过程中，2-MBT 会吸附在 AA 2024-T3 的表面上。未发现 2-MBT 和 Ce3+ 基缓蚀剂之间存在协同效应。建议 2-MBT 保护金属间化合物颗粒免受早期浸泡时的腐蚀，并阻止氢氧化铈在第二相颗粒上沉淀。在测试时间范围内，与 CeCl3 和 2-MBT+ CeCl3 相比，2-MBT 显示出更好的腐蚀防护性能。 (C) 2020 Elsevier B.V. 保留所有权利。
The corrosion protection mechanism of 2-mercaptobenzothiazole (2-MBT) and its potential synergistic effect with cerium chloride (CeCl3) for sustainability of the aerospace alloy AA 2024-T3 was investigated. The corrosion inhibitors 2-MBT and CeCl3 and their potential synergistic properties were assessed with image-assisted electrochemical noise, the split-cell technique, potentiodynamic polarization, electrochemical impedance spectroscopy (EIS) and scanning electron microscopy (SEM) observations. It is suggested that 2-MBT inhibits the dealloying of S-phase particles and prevents the formation of Cu-rich particles on the surface of AA 2024-T3. 2-MBT protects the second phase particles from corrosion and offers sustainability in 3.5% NaCl solution by formation of a protective layer on the surface of AA 2024-T3. Additionally, 2-MBT is adsorbed on the surface of AA 2024-T3 during anodic dissolution of aluminium. A synergistic effect between 2-MBT and the Ce3+ based corrosion inhibitor was not found. It is suggested that 2-MBT protects the intermetallic particles from corrosion from the early immersion time and blocks the precipitation of cerium hydroxides over the second phase particles. 2-MBT revealed better corrosion protection properties compared with CeCl3 and 2-MBT+ CeCl3 in the tested time scale. (C) 2020 Elsevier B.V. All rights reserved.