Flame retardancy and conductive properties of polyester fabrics coated with polyaniline
Flame retardancy and conductive properties of polyester fabrics coated with polyaniline
复制标题
DOI：
10.1177/0040517515606360
复制
发表时间：
2016-07-01
影响因子：
2.3
通讯作者：
Wei, Qufu
中科院分区：
文献类型：
--
作者：
Yu, Jian;Zhou, Tianchi;Wei, Qufu
Polyester fabrics were coated by polyaniline synthesized via in-situ chemical polymerization and doped with HCl and H3PO4. The coated fabrics were examined by scanning electron microscopy, infrared spectrum and thermogravimetric analysis. The performance of flame retardancy and conductivity of polyester fabrics were studied by Limiting Oxygen Index (LOI) and cyclic voltammetry measurements. Experimental results indicated that the modified polyester fabrics had both excellent flame retardancy and conductivity. The sample molar ratio of ammonium persulfate (APS) to aniline of 1.2:1 resulted in the highest conductivity of 17.8 s/cm and the highest LOI of 42 vol% was acquired at the molar ratio of aniline to APS of 1:2.